Constructing 3D flower-like LaFe bimetal oxides with abundant mesoporous and controllable active sites for high-efficient phosphorus removal: Synthesis, mechanism, and application

Bimetallic capture sites on porous La/Bi hydroxyl double salts for efficient phosphate adsorption: Multiple active centers and excellent selective properties

The rapid development of modern agriculture aggravated water eutrophication. Therein, efficient and selective removal of phosphorus in water is the key to alleviating eutrophication. It is well known that lanthanum (La)-based material is a kind of outstanding phosphorus-locking agent. Therefore, improving the property of La-based adsorbents is a hot topic in this field. Herein, novel porous hydroxyl double salts (La/Bi-HDS) with bimetallic capture sites were prepared. The experimental result shows that La/Bi-HDS could maintain the high removal rate in the solution with a higher concentration of competing ions and the maximum P adsorption quantity of La/Bi-HDS attains 168.12 mg/g. Mechanistic studies supported by density functional theory (DFT) calculation demonstrate that introducing Bi3+ optimizes the electronic structure of La, reducing adsorption energy. In addition, the surface analysis shows that the introduction of Bi, which increases the pore size and volume of the material, improves the utilization efficiency of the active site. In a word, the introduction of Bi element as a strategy of killing two birds with one stone successfully improved the performance of La-based adsorbent. It provided a new direction for developing an efficient phosphorus-locking agent.

Investigation on water defluoridation via batch and continuous mode using Ce-Al bimetallic oxide: Adsorption dynamics, electrochemical and LCA analysis

With variable atomic ratios, Ce-Al bimetallic oxides were fabricated using the sol-gel combustion method and utilized for efficient fluoride removal. The synthesized bimetallic oxides were extensively studied using advanced characterization techniques, including TGA, XRD, FTIR, BET surface area analysis, EDX-assisted FESEM, XPS and impedance analysis. These techniques facilitate the interpretation of the chemical and physical properties of the synthesized material. The Ce-Al (1:1) bimetallic oxide was selected as an adsorbent for the defluoridation. The Ce-Al (1:1) oxide demonstrates a moderately high surface area of 108.67 m²/g. The sorption behaviour of fluoride on Ce-Al (1:1) was thoroughly investigated using batch and column modes. The maximum fluoride removal efficiency (99.4%) was achieved at a temperature of 45 °C and pH of 7.0 using an adsorbent dose of 0.18 g/L for 35 min. Pseudo-second-order kinetic model appropriately describes the sorption process. Freundlich's adsorption isotherm was more pertinent in representing fluoride adsorption behaviour. The maximum fluoride adsorption capacity is 146.73 mg/g at 45 °C. Thermodynamics study indicates fluoride adsorption on Ce-Al (1:1) bimetallic oxide is spontaneous and feasible. The adsorption mechanism was interpreted through XPS spectra, indicating that the physisorption process is mainly responsible for fluoride adsorption. An in-depth investigation of the adsorption dynamics was carried out using mass transfer models and found that the external diffusion process limits the overall adsorption rate. An electrochemical investigation was performed to understand the effect of fluoride adsorption on the electrochemical behaviour of bimetallic oxide. The fixed-bed column adsorption study suggested that the lower flow rate and increased bed height favourably impacted the overall defluoridation process, and column adsorption results were suitably interpreted through both the Adam-Bohart model and Yoon-Nelson dynamics model. The sustainable aspect of the defluoridation process was elucidated in terms of carbon footprint measurement using life cycle assessment analysis. The carbon footprint of the entire treatment process was calculated as 0.094 tons/year.