Objective

A combination of self-etch and additional etch techniques as pre-cementation procedures for fiber post restoration was reported able to increase the bonding of adhesive material. This research aimed to determine the effects of different etching techniques on resin cement penetration into dentinal tubules.

Materials and methods

Thirty-two endodontic treated premolars were prepared for 10 mm fiber posts and were divided into two groups (n = 16). Group one was treated with self-etch only, and the second was treated with a combination of self-etch and additional etching. The fiber posts were cemented using fluorescent rhodamine B 0.1%-colored resin cement. The samples were cut to a 2 mm thickness in the middle third of the root and were evaluated with confocal laser scanning microscopy (CLSM). Statistical analysis measurements were analyzed by an independent t-test and Pearson correlation test.

Results

There were statistically different in densities hybrid layer and resin tag penetration lengths. Statistically strong linear positive correlations between the hybrid layer density and resin tag penetration length in both groups were also observed. Hybrid layer density (9.68 μm), resin tag penetration depth (32.51 μm) in the self-etch group with additional etching were higher than in the other group. The Pearson correlation test results between hybrid bond density and resin tag penetration depth in the self-etch treatment group showed a value of r = 0.634 and p-value = 0.008 and in the etching group self-treatment with additional etching a value of r = 0.516 and p-value = 0.041 (p ≤ 0.05).

Conclusion

There is a statistically significant positive correlation or linear relationship between hybrid bond density and the penetration depth of resin tags in both treatment groups: the thicker the hybrid layer density, the deeper the penetration of the resin tags. This phenomenon may increase mechanical strength regarding stronger binding of resin cement to a tooth’s substrate.

Sealability of Different Root Canal Nanosealers: Nano Calcium Hydroxide and Nano Bioactive Glass

Background:

The success of the endodontic treatment is largely dependent on the sealing achieved by root canal obturation. The application of sealer fills imperfections and increases adaptation of the root filling to the canal walls.

Aim:

To evaluate the sealability of experimental nanosealers (nano calcium hydroxide and nano bioactive glass) and to compare it with the commercial zinc oxide eugenol sealer using a dye penetration method.

Materials and Methods:

Sixty single-rooted mandibular premolars were selected. The tooth crowns were removed so as to obtain standardized 15-mm-long root specimens. The root canal was instrumented with Protaper Ni-Ti rotary file and the final file size was up to # F4/.06 (in vitro study). They were then randomly allocated into 3 groups of 20 specimens each (n=20) according to the sealer used for obturation, and all samples were filled with single cone gutta-percha (#40/06) and one of the tested sealers. All teeth were coated with nail polish and then suspended in 2% methylene blue dye for 7 days. Stereo-microscope (x10) was used to evaluate the sealability of newly introduced nanosealers. The data were statistically analyzed by ANOVA test followed by post hoc analysis (P < 0.05).

Results:

Significant improvement shown by the presented study suggests that nano calcium hydroxide sealer showed significantly less dye leakage than nano bioactive glass sealer and zinc oxide eugenol sealer.

Conclusion:

The results of this study showed that the synthesized nano-powder sealers are suitable for use in root canal therapy to prevent leakage.

The root canal can be sealed better by using smaller nano-powder particle sizes. In addition, the two groups exhibited significant differences in leakage in comparison with commonly used ZOE sealer.

Effect of Root Canal Sealers on Bond Strength of Fiber Posts to Root Dentin Cemented after one Week or six Months

Eugenol-based root canal sealers (RCS) have been widely used by clinicians; however, their effect on resinous materials is still questionable. The objective of this study was to evaluate the influence of RCS at 1 week and 6 months' post obturation on the bond strength (BS) of glass fiber posts (GFP) to root dentin, using conventional and self-adhesive cementation systems (CS). The roots of 56 extracted human canines, were divided in eight groups (n=7) according to the combination of the following factors: RCS (with or without eugenol-Endofill and Sealer 26, respectively), storage period post obturation and prior GFP cementation (1 week and 6 months) and cementation systems (Variolink II - conventional resin cement or RelyX U200-self-adhesive resin cement). After one week, the specimens were transversely sectioned into six 1-mm-thick disks and were subjected to the push out BS test. The data were subjected to 3-way ANOVA and Tukey's tests (α=0.05). The BS were not affected by the RCS, neither the CS (P>0.05). Just the period post obturation showed statistically significant differences (P 0.05), where the GFP cemented 6 months after the endodontic treatment showed higher values than those cemented 1 week after it.