Facile pore structure control of poly(vinylidene fluoride) membrane for oil/water separation

Antifouling BaTiO3/PVDF piezoelectric membrane for ultrafiltration of oily bilge water

Barium titanate/polyvinylidene fluoride (BaTiO₃/PVDF) piezoelectric membrane was successfully prepared and generated in-situ vibrations to reduce membrane fouling by applying alternating current (AC) signal for oily bilge water ultrafiltration. The effect of in-situ vibration on membrane fouling was investigated through changing in the excitation alternating voltage and its frequency, pH, crossflow rate. The results indicated that the piezoelectric membrane by applying AC signal remarkably alleviated the membrane fouling for bilge water ultrafiltration. The membrane fouling decreased with increasing the AC signal voltage. The final steady-state permeate flux from the piezoelectric membrane for bilge water ultrafiltration increased with the AC signal voltage, raising it by up to 63.4% at AC signal voltage of 20 V compared to that of the membrane without applying AC voltage. The high permeate flux was obtained at the resonant frequency of 220 kHz. During the 50-h ultrafiltration of bilge water with the piezoelectric membrane excited at 220 kHz and 15 V, the permeate flux from the membrane was stable. The oil concentration in outflow from the piezoelectric membrane was below 14 ppm, which met the discharged level required by IMO convention. The total organic carbon removal rate in bilge water was over 94%.

A Facile Method to Control Pore Structure of PVDF/SiO2 Composite Membranes for Efficient Oil/Water Purification

The use of poly(vinylidene fluoride) (PVDF) microfiltration (MF) membranes to purify oily water has received much attention. However, it is challenging to obtain high-performance PVDF microfiltration membranes due to severe surface fouling and rapid decline of permeability. This study explored a new approach to fabricate high-performance PVDF/silica (SiO₂) composite membrane via the use of a polymer solution featuring lower critical solution temperature (LCST) characteristics and the non-solvent thermally induced phase separation method (NTIPS). Coupling with morphological observations, the membrane formation kinetics were analyzed in depth to understand the synergistic effect between the LCST solution properties and fabrication conditions in NTIPS. Utilizing such a synergistic effect, the transition from finger-like macrovoid pores to bi-continuous highly connected pores could be flexibly tuned by increasing the PVDF concentration and the weight ratio of SiO₂/PVDF in the dope solution and by raising the coagulation temperature to above the LCST of the solution. The filtration experiments with surfactant-stabilized oil-water emulsion showed that the permeation flux of the PVDF/SiO₂ composite membranes was higher than 318 L·m^-2·h^-1·bar^-1 and the rejection above 99.2%. It was also shown that the PVDF/SiO₂ composite membranes, especially those fabricated above the LCST, demonstrated better hydrophilicity, which resulted in significant enhancement in the anti-fouling properties for oil/water emulsion separation. Compared to the benchmark pure PVDF membrane in oily water purification, the optimal composite membrane T70 was demonstrated via the 3-cycle filtration experiments with a significantly improved flux recovery ratio (F_rr) and minimal reduced irreversible fouling (R_ir). Overall, with the developed method in this work, facile procedure to tune the membrane morphology and pore structure was demonstrated, resulting in high performance composite membranes suitable for oil/water emulsion separation.

Freely switchable super-hydrophobicity and super-hydrophilicity of sponge-like poly(vinylidene fluoride) porous fibers for highly efficient oil/water separation

Highly efficient oil/water separation ability is a prerequisite for the actual application of the membranes in oily sewage treatment, which is closely related to the surface feature and the porous structure of the membranes. In this work, the electrospun poly(vinylidene fluoride) (PVDF) porous fibers were firstly fabricated through blend-electrospinning with poly(vinyl pyrrolidone) (PVP) and then treating in distilled water. The results showed that the fibers exhibited the sponge-like porous structure, and a few PVP was reserved in the fibers due to the relatively good interaction between PVDF and PVP. The fibrous membrane exhibited high porosity, super-wettability with freely switchable super-lipophilicity and super-hydrophilicity. The oil adsorption capacities as well as the oil and water fluxes were measured, and the oil adsorption capacities were varied in the range of 22.7-76.0 g/g, and oil and water fluxes were 54,737.3 and 56,869.9 L/(m²h), respectively. Specifically, the PVDF porous fibrous membranes showed excellent separation abilities and they could highly efficiently separate oil from oil-in-water emulsions or separate water from water-in-oil emulsions, accompanied with the extremely high water or oil flux. This work confirms that the PVDF membranes composed of the porous fibers can be used in wastewater treatment.