The optimized flow-electrode capacitive deionization (FCDI) performance by ZIF-8 derived nanoporous carbon polyhedron

ZIF-8-derived Zn, N-codoped porous carbon as a high-performance piezocatalyst for organic pollutant degradation and hydrogen production

The development of highly efficient piezocatalysts has attracted widespread attention for energy conversion and pollution abatement. This paper reports for the first time exceptional piezocatalytic properties of a Zn- and N-codoped porous carbon piezocatalyst (Zn-N_x-C) derived from the zeolitic imidazolium framework-8 (ZIF-8) for both hydrogen production and degradation of organic dyes. The Zn-N_x-C catalyst has a high specific surface area of 810.6 m²/g and retains the dodecahedron structure of ZIF-8. Under ultrasonic vibration, the hydrogen production rate of Zn-N_x-C has achieved 6.29 mmol/g/h, surpassing most recently reported piezocatalysts. Additionally, the Zn-N_x-C catalyst demonstrates a 94% degradation efficiency for organic rhodamine B (RhB) dye during 180 min of ultrasonic vibration. This work sheds new light on the potential of ZIF-based materials in the field of piezocatalysis and provides a promising avenue for future developments in the area.

Carbon Material-Based Flow-Electrode Capacitive Deionization for Continuous Water Desalination

Flow-electrode capacitive deionization (FCDI) offers an electrochemical, energy-efficient technique for water desalination. In this work, we report the study of carbon-based FCDI, which consists of one desalination chamber and one salination chamber and applies a carbon nanomaterials-based flow electrode that circulates between the cell anode and cathode, to achieve a fast, continuous desalination process. Five different carbon nanomaterials were used for preparing the flow electrode and were studied for the desalination performance, with properties including average salt removal rate (ASRR), salt removal efficiency (SRE), energy consumption (EC) and charge efficiency (CE) being quantitatively determined for comparation. Different FCDI parameters, including carbon concentration and flow rate of the flow electrode and cell voltage, were investigated to examine the influences on the desalination. Long-term operation of the carbon-based FCDI was evaluated using the optimal results found in the conditions of 1.5 M concentration, 1.5 V cell voltage, and 20 mL min−1 flow rate of electrode and water streams. The results showed an ASRR of 63.7 µg cm−2 min−1, EC of 162 kJ mol−1, and CE of 89.3%. The research findings validate a good efficiency of this new carbon-based FCDI technology in continuous water desalination and suggest its good potential for real, long-term application.

Regulating Surface Wettability and Charge Density of Porous Carbon Particles by In Situ Growth of Polyaniline for Constructing an Efficient Electrical Percolation Network in Flow-Electrode Capacitive Deionization

Both electrical conductivity and surface wettability are required for the selection of active carbon materials in flow-electrode capacitive deionization, while a trade-off exists between these two properties. In this work, a hybrid material with a thin layer of polyaniline (PANI) coating on activated carbon (AC/PANI) was successfully developed to retain excellent electrical conductivity and acquire good surface wettability. By adjusting the dosage of initiator, AC/PANI composites with different loading fractions of PANI were obtained. The electrochemical testing demonstrated that the AC/PANI composites have higher specific capacitance and lower ion diffusion resistance compared to pure AC, resulting in better desalinization performance. Specifically, with a feed concentration of 1600 mg/L, excellent adsorption capacity and high charge efficiency can be simultaneously achieved at 13.51 mg/g and 92.21%, respectively. Benefiting from the formation of a continuous electrical percolation network and reduced solid/liquid interfacial transport resistance, a 39% enhancement of average salt adsorption rate (from 0.54 to 0.75 μmol/min/cm²) was obtained.