Enrichment of 1, 4-dioxane from water by sweep gas membrane distillation on nano-carbon immobilized membranes

Development of a Carbon Nanotube-Enhanced FAS Bilayer Amphiphobic Coating for Biological Fluids

This study reports the development of a novel amphiphobic coating. The coating is a bilayer arrangement, where carbon nanotubes (CNTs) form the underlayer and fluorinated alkyl-silane (FAS) forms the overlayer, resulting in the development of highly amphiphobic coatings suitable for a wide range of substrates. The effectiveness of these coatings is demonstrated through enhanced contact angles for water and artificial blood plasma fluid on glass, stainless steel, and porous PTFE. The coatings were characterized using Fourier-transform infrared spectroscopy (FTIR), scanning electron microscopy (SEM), thermogravimetric analysis (TGA), atomic force microscopy (AFM), and contact angle (CA) measurements. The water contact angles achieved with the bilayer coating were 106 ± 2°, 116 ± 2°, and 141 ± 2° for glass, stainless steel, and PTFE, respectively, confirming the hydrophobic nature of the coating. Additionally, the coating displayed high repellency for blood plasma, exhibiting contact angles of 102 ± 2°, 112 ± 2°, and 134 ± 2° on coated glass, stainless steel, and PTFE surfaces, respectively. The presence of the CNT underlayer improved plasma contact angles by 29%, 21.7%, and 16.5% for the respective surfaces. The presence of the CNT layer improved surface roughness significantly, and the average roughness of the bilayer coating on glass, stainless steel, and PTFE was measured to be 488 nm, 301 nm, and 274 nm, respectively. Mechanistically, the CNT underlayer contributed to the surface roughness, while the FAS layer provided high amphiphobicity. The maximum effect was observed on modified glass, followed by stainless steel and PTFE surfaces. These findings highlight the promising potential of this coating method across diverse applications, particularly in the biomedical industry, where it can help mitigate complications associated with device-fluid interactions.

Reduction and Elimination of Humic Acid Fouling in Air Sparged Membrane Distillation Using Nanocarbon Immobilized Membrane

In this paper, we present the treatment of humic acid solution via carbon nanotube immobilized membrane (CNIM) distillation assisted by air sparging (AS). Carbon nanotubes offer excellent hydrophobicity to the modified membrane surface and actively transport water vapor molecules through the membrane to generate higher vapor flux and better rejection of humic acid. The introduction of air sparging in the membrane distillation (MD) system has changed the humic substance fouling by changing the colloidal behavior of the deposits. This modified MD system can sustain a higher run time of separation and has enhanced the evaporation efficiency by 20% more than the regular membrane distillation. The air sparging has reduced the deposition by 30% in weight and offered lesser fouling of membrane surface even after a longer operating cycle. The water vapor flux increased with temperature and decreased as the volumetric concentrating factor (VCF) increased. The mass transfer coefficient was found to be the highest for the air sparged—carbon nanotube immobilized membrane (AS-CNIM) integrated membrane distillation. While the highest change in mass transfer coefficient (MTC) was found for polytetrafluoroethylene (PTFE) membrane with air sparging at 70 °C.