Reduced shrinkage and mechanically strong dual-network polyimide aerogel films for effective filtration of particle matter

Binary Polyamide-Imide Fibrous Superelastic Aerogels for Fire-Retardant and High-Temperature Air Filtration

Fibrous air filtration materials are highly desirable for particle removal from high-temperature emission sources. However, the existing commercial filter materials suffer from either low filtration efficiency or high pressure drop, due to the difficulty in achieving small fiber diameter and high porosity simultaneously. Herein, we report a facile strategy to fabricate mechanical robust fibrous aerogels by using dual-scale sized PAI/BMI filaments and fibers, which are derived from wet spinning and electrospinning technologies, respectively. The creativity of this design is that PAI/BMI filaments can serve as the enhancing skeleton and PAI/BMI fibers can assemble into high-porosity interconnected networks, enabling the improvement of both mechanical property and air filtration performance. The resultant dual-scale sized PAI/PBMI fibrous aerogels show a compressive stress of 8.36 MPa, a high filtration efficiency of 90.78% (particle diameter of 2.5 μm); for particle diameter over 5 μm, they have 99.99% ultra-high filtration efficiency, a low pressure drop of 20 Pa, and high QF of 0.12 Pa^-1, as well as thermostable and fire-retardant properties (thermal decomposition temperature up to 342.7 °C). The successive fabrication of this material is of great significance for the govern of industrial dust.

The Aramid-Coating-on-Aramid Strategy toward Strong, Tough, and Foldable Polymer Aerogel Films

Aerogel has been much highlighted as an emerging lightweight thermal insulation material, but problems such as fragility, low strength, liquid permeability, and lack of flexibility greatly limit further applications. In this work, a facile aramid-coating-on-aramid (ACoA) method is demonstrated to fabricate all-aramid aerogel composite films for thermal insulation. The method started from the bottom-up synthesis of polymerization-induced para-aramid nanofibers (PANF), which were easily transformed into aerogel films through the vacuum-assisted filtration followed by the freeze-drying techniques. Then, the heterocyclic aramid (HA) solution prepared through the low-temperature-solution polycondensation was used as the coating to be applied onto the PANF aerogel films, and composite films of HA/PANF aerogel were simply achieved with HA contributed to the dense and continuous surface layer. The bulk HA film is of superior mechanical and thermal properties to those of the PANF film. Moreover, reliable interfacial interlocking structures were developed beneath the outermost surface via the interpenetration of the infiltrated HA with PANF network. The comprehensive result was the 15 times enhanced tensile strength, 33 times enhanced fracture toughness, the high thermal decomposition temperature, and the additional flexibility for the foldable films of HA/PANF aerogel. The sealing of the surface macropores greatly suppressed the surface chalking and high water absorption. However, the survival of the tiny pores inside the composite maintained the low enough level of the thermal conductivity to provide effective protections against high temperature not only in air but also under wet or even liquid conditions, suggesting the broader applications for thermal insulation.