Simplified sonochemical preparation of titania embedded with selected metals for purification of benzene and toluene

Fabrication of a Cu2O-Au-TiO2 Heterostructure with Improved Photocatalytic Performance for the Abatement of Hazardous Toluene and α-Pinene Vapors

In the current research, a Cu2O-Au-TiO2 heterostructure was fabricated via a step-wise photodeposition route to determine its possible application in the photocatalytic oxidation of hazardous vapors. The results of electron microscopy and X-ray photoelectron spectroscopy confirm the successful fabrication of the Cu2O-Au-TiO2 heterostructure. Strong absorption in the visible region, along with a slight red-shift in the absorption edge, was observed in the UV–vis diffuse reflectance spectrum of Cu2O-Au-TiO2 composite, which implies that the composite can generate a greater number of photoexcited charges necessary for photocatalytic reaction. Toluene and α-pinene, as common gas contaminants in the indoor atmosphere, were employed to assess the photooxidation efficiency of the Cu2O-Au-TiO2 composite. Importantly, photocatalytic activity results indicate that the Cu2O-Au-TiO2 composite showed excellent photodegradation performance compared to pure TiO2 and Cu2O-TiO2 and Au-TiO2, where photocatalytic efficiency was approximately 92.9% and 99.9% for toluene and α-pinene, respectively, under standard daylight illumination. The increased light-harvesting capacity and boosted separation efficiency of electron-hole pairs were mainly accountable for improved degradation performance of the Cu2O-Au-TiO2 composite. In addition, the degradation efficiencies for toluene and α-pinene by the Cu2O-Au-TiO2 composite were also examined under three different light sources: 0.32 W white, blue and violet LEDs. The findings of this work suggested a great promise of effective photooxidation of gas pollutants by the Cu2O-Au-TiO2 composite.

Sonochemical Synthesis of Ce-doped TiO2 Nanostructure: A Visible-Light-Driven Photocatalyst for Degradation of Toluene and O-Xylene

Ce-doped TiO2 nanostructures (CeT) with different amounts of Ce (0.5, 0.75, 1.0, 1.5, and 2.0 wt.%) were synthesized using a sonochemical processing method. The physicochemical properties of the prepared samples were explored using UV-visible diffuse reflectance spectroscopy (UV-vis DRS), field-emission TEM (FE-TEM), XRD, X-ray photoelectron spectroscopy (XPS), photoluminescence spectroscopy (PL), and surface area and pore size analyzers. The photocatalytic performance of the prepared CeT was assessed by monitoring their degradation efficiencies for gaseous toluene and o-xylene-widely known as significant indoor air pollutants-under daylight irradiation. The prepared CeT exhibited significantly improved photocatalytic performance towards the degradation of toluene and o-xylene, which was much higher than that observed for pure TiO2 and commercial P25 TiO2. Particularly, photocatalytic degradation efficiencies by the prepared CeT catalysts increased remarkably in the case of o-xylene (up to 99.4%) compared to toluene (up to 49.1%). The degradation efficiency by the CeT was greatest for the CeT-0.75 sample, followed by, in order, CeT-1.0, CeT-0.5, CeT-1.5, and CeT-2.0 samples in agreement with the order of the surface area and the particle size of the catalysts. According to the change of light source, the average decomposition efficiencies for toluene and o-xylene by CeT-0.75 were shown in the order of conventional daylight lamp > violet light emitting diodes (LEDs) > white LEDs. The decomposition efficiencies normalized to supplied electric power, however, were estimated to be in the following order of violet LEDs > white LEDs > conventional daylight lamp, indicating that the LEDs could be a much more energy efficient light source for the photodecomposition of target toluene and o-xylene using the CeT-0.75 photocatalyst.

The role of potassium chlorate on expansion of dickite layers and the preparation of a novel TiO2 impregnated dickite photocatalyst using expanded dickite as carrier

The layered dickite particles were expanded by rapidly heating the mixture of dickite–urea intercalation complex and KClO₃.