Effects of pulsatile versus non-pulsatile pulpal pressure simulations on diffusional transport across human dentine in vitro

The effect of simulated intrapulpal pressure on bond strength to enamel and dentine

The purpose of this study was to evaluate the effect of simulated intrapulpal pressure on the shear bond strength (SBS) of a self-etching bonding system (Clearfil Liner Bond II) to both enamel and dentine surfaces. Forty-two caries-free human molar teeth were randomly assigned to two equal groups (n=21). One group of 21 teeth was connected to a special pulpal pressure machine, which is developed to simulate in vivo conditions. The buccal and lingual surfaces of the teeth were prepared with a diamond wheel to create flat dentine and enamel surfaces. A self-etching bonding system was then applied under pulpal pressure and 2.5 mm diameter composite cylinders were bonded to the prepared surfaces. The samples were then stored in distilled water at room temperature for 24 h under pulpal pressure before SBS was tested. The second restored group was used as a control and the teeth were not connected to the pulpal pressure apparatus during material application and test procedures. They were stored for 24 h in distilled water at room temperature before the SBS test. Fracture analysis of the enamel and dentinal surfaces was performed using a stereomicroscope. Shear bond strength values to dentine was significantly reduced with pulpal pressure (P < 0.001). However, in the enamel, SBS was increased (P < 0.001). In the control group, the SBS values to dentine and enamel did not show any significant difference (P > 0.05). Based on these results, it can be concluded that further analysis of enamel histology and bonding mechanisms are needed.

Eugenol diffusion through dentin related to dentin hydraulic conductance

OBJECTIVES

The purpose of this study was (1) to find an easy way of evaluating the concentration of eugenol in cell culture fluids; (2) to confirm the relationship between the concentration and the cytotoxicity of eugenol in vitro; (3) to evaluate the cytotoxicity of four temporary eugenol-based filling materials: IRM, super EBA, Kalsogen and zinc oxide-eugenol cement; and (4) to establish a relationship between dentin permeability, eugenol diffusion and cytotoxicity.

METHODS

(1) The concentration of eugenol was measured with a spectrofluorimeter; (2) the cell viability of L 929 cells cultivated for 24 h with eugenol-containing medium was evaluated by the MTT assay; (3) after measurement of hydraulic conductance, occlusal cavities in human teeth in vitro were filled with the restorative materials. The cytotoxicity was measured with undiluted test medium and with various dilutions in culture medium; (4) after Lp measurement, the eugenol concentration in the media in the pulp chamber that diffused from IRM and 10(3) mol/l eugenol solution was measured.

RESULTS

(1) A proportional relationship (p = 0.001 and r = 1) was found between the concentration of eugenol; (2) eugenol started to be cytotoxic at 10(-5) mol/l and killed 95% of the cells at 10(-3) mol/l; (3) zinc oxide-eugenol cement was the most cytotoxic filling material when tested with the 1:100 dilution; (4) a significant relationship was found between Lp and cytotoxicity (p = 0.04) depending on the dilution of the test medium. A significant relationship was found between Lp and eugenol diffusion from a 10(-3) mol/l solution (p = 0.03) but not between Lp and eugenol diffusing from solid IRM (non significant).

SIGNIFICANCE

Eugenol diffusion from zinc oxide-eugenol cement appears to depend more on the role of hydrolysis of eugenol from zinc oxide-eugenol cement than on dentin permeability.