Effect of four acrylic bone cements on transforming growth factor-beta1 expression by osteoblast-like cells MG63

Physicochemical, Mechanical, and Biological Properties of Bone Cements Prepared with Functionalized Methacrylates

Bone cements prepared with methyl methacrylate (MMA) as a base monomer and either methacrylic acid (MAA) or diethyl amino ethyl methacrylate (DEAEMA) as comonomers were characterized in terms of curing behavior, mechanical properties, and their in vitro biocompatibility.

The curing time and setting temperature were found to be composition dependent while the residual monomer was not greatly affected by the presence of either acidic or alkaline comonomers in the bone cements. For samples with MAA comonomer, a faster curing time and higher setting temperature were observed when compared to the cement with DEAEMA comonomer.

In terms of mechanical properties, the highest compressive strength was exhibited by formulations containing MAA, while the highest impact strength was shown by the formulations prepared with DEAEMA. There were no differences observed between the two formulations for tensile, shear, and bending strength values. Similarly, fatigue crack propagation studies did not reveal differences with the addition of either DEAEMA or MAA.

No differences were observed in the initial number of attached primary rat femur osteoblasts on the different bone cements and positive controls. However, after 48 h there was a reduced proliferation in the cells grown on bone cements containing MAA.

Growth factors in bone repair

The role of growth factors (GF) in bone repair is widely recognised, particularly for bone morphogenetic proteins (BMPs), fibroblast growth factor (FGF), insulin-like growth factors (IGFs), platelet-derived growth factor (PDGF), transforming growth factor-beta (TGF-beta) and vascular endothelial growth factor (VEGF). GF are usually stored in the extracellular matrix (ECM), but after injury are actively released by ECM, cells and platelets. In this paper, the use of different recombinant GF for bone repair stimulation is summarised in experimental research and clinical applications. Drug delivery systems, including carriers, cell or gene therapy, are needed to ensure a sustained local release of the factors, but efficacy and potential side effects of such systems require additional research prior to clinical applications. Current sources for delivery of a GF mixture into the site of bone repair are platelet gel and demineralised bone matrix. Nevertheless, the levels of GF in such preparations are affected by variability among donors and differences in preparation. Autogenous GF, produced by the patient himself during the bone repair process, potentially interfere with prosthetic devices or even have a role in implant loosening due to the periprosthetic tissue reaction. In conclusion, GF are key components of functional bone regeneration: screening of basic research results and controlled clinical trials are accelerating the development of GF in orthopaedic surgery.

Biological response of new activated acrylic bone cements with antiseptic properties. Histomorphometric analysis

The biological response to an acrylic bone cement cured with 4,4'-bis-dimethylamino benzydrol (BZN) as activator of reduced cytotoxicity and antiseptic properties, has been carried out and compared with that obtained for CMW 3 cement. Histomorphometrical data (undecalcified trichromic Goldner staining) were obtained by measuring the most significant variables at the bone-cement interface. Quantitative results of tissue response revealed that newly formed bone and connective tissue were maximum at 4 weeks whereas bone marrow increased with time of implantation for both cements. Statistical analysis (p < 0.05) showed no significant differences in newly formed bone and bone marrow with time and between both groups, however, connective tissue significantly decreased between 4 weeks and 12 weeks for BZN cement, and between 12 weeks and 24 weeks for CMW3. By comparing both cements at each time, lower significant percentage of connective tissue at the bone-cement interface of the BZN cement, was obtained at 12 and 24 weeks, however, a very low amount of connective tissue was found for both cements. All the results indicate that the new activated system could be applied clinically in a relatively short time, after the corresponding preclinical study.

Surface characterisation of various bone cements prepared with functionalised methacrylates/bioactive ceramics in relation to HOB behaviour

This study reports the relationship between the biocompatibility and surface properties of experimental bone cements. The effect of hydroxyapatite (HA) or alpha-tri-calcium phosphate (alpha-TCP) incorporated into bone cements prepared with methyl methacrylate as base monomer and either methacrylic acid or diethyl amino ethyl methacrylate (DEAEMA) as comonomers was investigated. The in vitro biocompatibility of these composite cements was assessed in terms of the interaction of primary human osteoblasts grown on the materials over a period of 5 days and compared with a control surface. These results were related to the surface properties investigated through a number of techniques, namely Fourier transform infrared, contact angle measurements, X-ray photoelectron spectroscopy and energy dispersive analysis of X-rays. Complementary techniques of thermal analysis and ion chromatography were also performed. Biocompatibility results showed that the addition of alpha-TCP improves biocompatibility regardless of comonomer type. This is in contrast to HA-based cements where cell proliferation was significantly lower. Surface characterisations showed that structural integrity of the materials was maintained in the presence of the acid and base comonomers, and water contact angles were reduced particularly in DEAEMA containing materials. Furthermore, ion chromatography confirmed higher Ca2+ and PO4(3-) ion release by both types of ceramics, particularly for those containing DEAEMA. In conclusion, the incorporation of acidic and basic comonomers to either HA or alpha-TCP ceramics containing bone cements can have differential effects upon the attachment and proliferation of bone cells in vitro. Moreover, those cements consisting of alpha-TCP and containing DEAEMA comonomer indicated the most favourable biocompatibility.