Effect of CeO2-ZrO2 on Pt/C electrocatalysts for alcohols oxidation

An Electrochemical Investigation of Methanol Oxidation on Thin Films of Nickel Oxide and Its Composites with Zirconium and Yttrium Oxides

The present work is focused on the fabrication of NiO-ZrO2/FTO and NiO-Y2O3/FTO thin films via a simple dip-coating method. The films are deposited from precursor solutions of Ni(CH3COO)2·2H2O, Zr(CH3COO)4, Y(CH3COO)3·H2O in methanol. The synthesized films, after proper characterization, are employed for electrochemical oxidation of methanol. The analytical techniques such as X-ray diffraction (XRD), Raman, and Infrared (IR) spectroscopy reveal the successful formation of crystalline thin films of mixed metal oxide without any additional impurities. Further, X-ray photoelectron spectroscopy (XPS) results, confirm the composition and oxidation state of all the elements present in thin films. The field emission scanning electron microscopy (FESEM) further aided to identify the uniformity and porous nature of composite thin films while the energy-dispersive X-ray spectroscopy (EDS) confirms the targeted elemental composition of the prepared thin films is in good agreement with precursors. The electrochemical oxidation of methanol results reveals that NiO-Y2O3/FTO and NiO-ZrO2/FTO thin films showed current densities of 6.2 mA/cm2 and 10 mA/cm2 at 0.65 V, respectively, against Ag/AgCl/3M KCl using 0.6 M methanol solution. Furthermore, Chronoamperometric (CA) results show good stability of NiO-ZrO2/FTO and NiO-Y2O3/FTO thin films with observed current decay of 10% and 6.8% of the initial current density, respectively. Moreover, the effect of scan rate and concentration of metals in a catalyst was also investigated. The Electrochemical impedance studies (EIS) further support electrochemical results, where the lower charge transfer resistance (Rct) values are recorded for composite thin films as compared to the pure metal oxide thin films (NiO/FTO, ZrO2/FTO, and Y2O3/FTO).

Ethanol Electrooxidation at Platinum-Rare Earth (RE = Ce, Sm, Ho, Dy) Binary Alloys

Proton exchange membrane fuel cells and direct alcohol fuel cells have been extensively studied over the last three decades or so. They have emerged as potential systems to power portable applications, providing clean energy, and offering good commercial viability. Ethanol is considered one of the most interesting fuels in this field. Herein, platinum-rare earth (Pt-RE) binary alloys (RE = Ce, Sm, Ho, Dy, nominal composition 50 at.% Pt) were produced and studied as anodes for ethanol oxidation reaction (EOR) in alkaline medium. A Pt-Dy alloy with nominal composition 40 at.% Pt was also tested. Their electrocatalytic performance was evaluated by voltammetric and chronoamperometric measurements in 2 M NaOH solution with different ethanol concentrations (0.2–0.8 M) in the 25–45 °C temperature range. Several EOR kinetic parameters were determined for the Pt-RE alloys, namely the charge transfer and diffusion coefficients, and the number of exchanged electrons. Charge transfer coefficients ranging from 0.60 to 0.69 and n values as high as 0.7 were obtained for the Pt0.5Sm0.5 electrode. The EOR reaction order at the Pt-RE alloys was found to vary between 0.4 and 0.9. The Pt-RE electrodes displayed superior performance for EOR than bare Pt, with Pt0.5Sm0.5 exhibiting the highest electrocatalytic activity. The improved electrocatalytic activity in all of the evaluated Pt-RE binary alloys suggests a strategy for the solution of the existing anode issues due to the structure-sensitive EOR.

Probing the spontaneous reduction mechanism of platinum ions confined in the nanospace by X-ray absorption fine structure spectroscopy

The reduction mechanism of Pt⁴⁺ ions confined in the channel of multi-walled carbon nanotubes was mainly investigated using X-ray absorption fine structure (XAFS) spectroscopy, with the aid of TEM, Raman, XRD and ICP-AES studies.