Pt/MoO3-WO3/CNTs catalyst with excellent performance for methanol electrooxidation

Preparation of Carbon Nanotubes with Supported Metal Oxide Nanoparticles: Effect of Metal Precursor on Thermal Decomposition Behavior of the Materials

To develop new catalysts based on carbon nanomaterials with supported metal oxide nanoparticles for oxidative transformations of sulfur compounds, a series of metal oxide nanoparticle-decorated carbon nanotubes (MOx/CNTs) were prepared by incipient wetness impregnation at a variation of the active metal type (M = Ce, Mo, Cu). The thermal decomposition of bulk and CNT supported metal precursors used in the preparation of MOx/CNTs was analyzed under inert atmosphere employing several thermoanalytical techniques (thermogravimetry, differential thermogravimetry and differential scanning calorimetry) coupled with mass spectrometry. The thermolysis parameters of the bulk and supported metal precursors were compared and the effect of CNT support on the decomposition pattern of compounds was elucidated. It was established that the decomposition of metal precursors supported on CNTs was started and completed at temperatures of 15‒25 and 25‒70 °C lower, respectively, compared with the bulk active metal precursor. The enhancement of CNT support stability against thermal degradation is observed in the following row of metal cations: Ce < Cu < Мо < pristine and metal anions of precursor: nitrate < chloride < sulfate. The optimal mode of thermal treatment of catalyst and appropriate active metal precursors were selected for advanced synthesis of nanosized MOx/CNT catalyst.

Facile synthesis of Pt nanoparticles supported on anatase TiO2 nanotubes with good photo-electrocatalysis performance for methanol

A Pt/TNTs/C catalyst showed enhanced MOR performance under the light illumination.

TiO2 Nanotube-Carbon (TNT-C) as Support for Pt-based Catalyst for High Methanol Oxidation Reaction in Direct Methanol Fuel Cell

In this study, TiO₂ nanotubes (TNTs) were synthesized via a hydrothermal method using highly concentrated NaOH solutions varying from 6 to 12 M at 180 °C for 48 h. The effects of the NaOH concentration and the TNT crystal structure on the performance for methanol oxidation were investigated to determine the best catalyst support for Pt-based catalysts. The results showed that TNTs produced with 10 M NaOH exhibited a length and a diameter of 550 and 70 nm, respectively; these TNTs showed the best nanotube structure and were further used as catalyst supports for a Pt-based catalyst in a direct methanol fuel cell. The synthesized TNT and Pt-based catalysts were analysed by FESEM, TEM, BET, EDX, XRD and FTIR. The electrochemical performance of the catalysts was investigated using cyclic voltammetry (CV) and chronoamperometric (CA) analysis to further understand the methanol oxidation in the direct methanol fuel cell (DMFC). Finally, the result proves that Pt-Ru/TNT-C catalyst shows high performance in methanol oxidation as the highest current density achieved at 3.3 mA/cm² (normalised by electrochemically active surface area) and high catalyst tolerance towards poisoning species was established.