Formaldehyde catalytic oxidation over hydroxyapatite modified with various organic molecules

Catalytic Oxidation of HCHO over the Sodium-Treated Sepiolite-Supported Rare Earth (La, Eu, Dy, and Tm) Oxide Catalysts

The sodium-treated sepiolite (NaSep)-supported rare earth oxide (RE/NaSep; RE = La, Eu, Dy, and Tm) samples were prepared using the rotary evaporation method. Physicochemical properties of these materials were characterized by XRD, SEM, BET, FTIR, XPS, H2–TPR, NH3–TPD, and in situ DRIFTS, and their catalytic activities for formaldehyde (HCHO) (2000 ppm) oxidation were evaluated. The results show that loading of the rare earth oxide on NaSep improved its catalytic performance. Among all the samples, Eu/NaSep performed the best, and complete HCHO conversion was achieved at a temperature of 150 °C and a gas hourly space velocity of 240,000 mL/(g h); a good catalytic activity was still maintained after 45 h of stability test. The catalytic oxidation mechanism of HCHO was studied using the in situ DRIFTS technique. As a result, the effective and stable catalytic performance of the Eu/NaSep sample was mainly due to the presence of hydroxyl groups on the sepiolite surface and the doped rare earth oxides, which contributed to its high performance. HCHO oxidation underwent via the steps of HCHO + O2 → HCOO− + OH− → H2O + CO2. It is concluded that the optimal catalytic activity of Eu/NaSep was associated with the highest Oads/Olatt atomic ratio, the largest amount of hydroxyl groups, the highest acidity, and the best reducibility. The present work may provide new insights into the application in the removal of high-concentration HCHO over the rare earth oxides supported on natural low-cost clays.

Hydroxyapatite, a multifunctional material for air, water and soil pollution control: A review

Hydroxyapatite (Ca₁₀(PO₄)₆(OH)₂), a calcium phosphate biomaterial, is a very promising candidate for the treatment of air, water and soil pollution. Indeed, hydroxyapatite (Hap) can be extremely useful in the field of environmental management, due in one part to its particular structure and attractive properties, such as its great adsorption capacities, its acid-base adjustability, its ion-exchange capability and its good thermal stability. Moreover, Hap is able to constitute a valuable resource recovery route. The first part of this review will be dedicated towards presenting Hap's structure and defining properties that result in its viability as an environmental remediation material. The second will focus on its use as adsorbent for wastewater and soil treatment, while indicating the mechanisms involved in this remediation process. Finally, the last part will impart all findings on Hap's applications in the field of catalysis, whether it be as catalyst, as photocatalyst, or as active phase support. Hence, all of the above will have served in showcasing the benefits gained by employing hydroxyapatite in air, water and soil clean-up.

Hydroxyapatite-Supported Low-Content Pt Catalysts for Efficient Removal of Formaldehyde at Room Temperature

Indoor environmental quality directly affects the life quality and health of human beings, and therefore, it is highly vital to eliminate the volatile organic compounds especially formaldehyde (HCHO), which is regarded as one of the most common harmful pollutants in indoor air. Hydroxyapatite (HAP)-supported Pt (Pt/HAP) catalysts with a low content of Pt (0.2 wt %) obtained via hydrothermal and chemical reduction processes could effectively remove gaseous HCHO from the indoor environment at room temperature. The influence of modifier in the preparation on the catalyst activity was investigated. The HAP and HAP modified by sodium citrate and hexamethylenetetramine-supported 0.2 wt % Pt could completely decompose HCHO into CO2 and water, while HAP modified by sodium dodecyl-sulfate-supported Pt removed HCHO primarily via adsorption. The HAP modified by the sodium citrate catalyst exhibited superior catalytic performance of HCHO compared to the HAP and HAP modified by hexamethylenetetramine and sodium dodecyl-sulfate-supported Pt catalysts, which was mainly because of its higher surface Ca/P ratio providing more Lewis acidic sites (Ca2+) for co-operational capture of HCHO molecules and a larger amount of active oxygen species. Our results indicate that an optimized combination of functional supports and low-content noble metal nanoparticles could be a route to fabricate effective room-temperature catalysts for potential application in indoor air purification.