Binary Fe/Mn-Based Nanocomposites as Li-Free Cathode Materials for Li Batteries Assembled in Charged State

Fluorinated Materials as Positive Electrodes for Li- and Na-Ion Batteries

Fluorine is known to be a key element for various components of batteries since current electrolytes rely on Li-ion salts having fluorinated ions and electrode binders are mainly based on fluorinated polymers. Metal fluorides or mixed anion metal fluorides (mainly oxyfluorides) have also gained a substantial interest as active materials for the electrode redox reactions. In this review, metal fluorides for cathodes are considered; they are listed according to the dimensionality of the metal fluoride subnetwork. The synthesis conditions and the crystal structures are described; the electrochemical properties are briefly indicated, and the nature of the electron transport agent is noted. We stress the crucial importance of the elaboration processes to induce the presence of cation disorders, of anion substitutions (mainly F-/O2- or F-/OH-) or vacancies. Finally, we show that an accurate structural characterization is a key step to enable enhanced material performances to overcome several lasting roadblocks, namely the large irreversible capacity and poor energy efficiency that are frequently encountered.

Li/Na Ion Storage Performance of a FeOF Nano Rod with Controllable Morphology

Although the conversion material iron oxyfluoride (FeOF) possesses a high theoretical specific capacity as a cathode material for Li/Na ion batteries, its poor rate and cycling performances, caused mainly by sluggish (Li+/Na+) reaction kinetics, restrict its practical application. Herein, FeOF with high purity, a fusiform nanorod shape and high crystallinity is prepared through a facile chemical solution reaction. The electrochemical measurements show that the present FeOF exhibits high capacity and good cycling stability as a cathode material for Li-ion batteries. Capacities of 301, 274, 249, 222, and 194 mAh/g at stepwise current densities of 20, 50, 100, 200, and 400 mA/g are achieved, respectively. Additionally, the capacity at 100 mA/g retains 123 mAh/g after 140 cycles. Meanwhile, as a cathode material for Na ion battery, it delivers discharge capacities of 185, 167, 151, 134 and 115 mAh/g at stepwise current densities of 20, 50, 100, 200, and 400 mA/g, respectively. A discharge capacity of 83 mAh/g at 100 mA/g is achieved after 140 cycles. The excellent lithium/sodium-storage performance of the present FeOF material is ascribed to its unique nanostructure.