Alumina-Supported Nickel onto Cordierite Monoliths for Ethane Oxidehydrogenation: Coating Strategies and Their Effect on the Catalytic Behavior

Synthesis of Co,Ce Oxide Nanoparticles Using an Aerosol Method and Their Deposition on Different Structured Substrates for Catalytic Removal of Diesel Particulate Matter

The synthesis of Co and Ce oxide nanoparticles using precipitation of precursor salt solutions in the form of microdroplets generated with a nebulizer proved to be an efficient, fast and inexpensive method. Different morphologies of single oxides particles were obtained. Ceria nanoparticles were almost cube-shaped of 8 nm average size, forming 1.3–1.5 μm aggregates, whereas cobalt oxide appeared as rounded-edged particles of 37 nm average size, mainly forming nanorods 50–500 nm. Co3O4 and CeO2 nanoparticles were used to generate structured catalysts from both metallic (stainless steel wire mesh monoliths) and ceramic (cordierite honeycombs) substrates. Ceria Nyacol was used as a binder to favor the anchoring of catalytic particles thus enhancing the adhesion of the coating. The resulting structured catalysts were tested for the combustion of diesel soot with the aim of being used in the regeneration of particulate filters (DPFs). The performance of these structured catalysts was similar to or even better than that exhibited by the catalysts prepared using commercial nanoparticles. Among the catalysts tested, the structured systems using ceramic substrates were more efficient, showing lower values of the maximum combustion rate temperatures (TM = 410 °C).

Tuning the selectivity of CO2 hydrogenation using ceramic hollow fiber catalytic modules

The unique structural features and advantageous pore distributions of alumina hollow fibers can be exploited to tune the selectivity in heterogeneous catalysis.

FeCrAlloy Monoliths Coated with Ni/Al2O3 Applied to the Low-Temperature Production of Ethylene

This paper investigates the oxidative dehydrogenation of ethane to produce ethylene at low temperatures (500 °C) in metallic structured substrates. To check this point, the FeCrAlloy® monoliths with different channel sizes (289–2360 cpsi) were prepared. The monoliths were coated with a Ni/Al2O3 catalyst (by washcoating of alumina and the latter nickel impregnation) and characterized by Scanning Electron Microscopy and Energy-Dispersive X-ray analysis (SEM-EDX), Temperature-Programmed Reduction (TPR), X-ray Diffraction (XRD) and X-ray Photoelectron Spectroscopy (XPS). The catalytic results showed that all monoliths coated with ~300 mg of catalyst presented similar ethane conversion (15%) at 450 °C. However, the lowest selectivity to ethylene was found for the monolith with the lower channel size and the higher geometric surface area, where a heterogeneous catalyst layer with Ni enriched islands was generated. Therefore, it can be said that the selectivity to ethylene is linked to the distribution of Ni species on the support (alumina). Nevertheless, in all cases the selectivity was high (above 70%). On the other hand, the stability in reaction tests of one of the coated monoliths was done. This structured catalyst proved to be more stable under reaction conditions than the powder catalyst, with an initial slight drop in the first 8 h but after that, constant activity for the 152 h left.