Mesoporous Carbon Beads Impregnated with Transition Metal Chlorides for Regenerative Removal of Ammonia in the Atmosphere

Polyester conversion by homogeneous catalysis for separating and recycling ammonia from biogas

Biogas is being promoted as a renewable and clean energy source. However, NH3 is a precursor of NOx and PM2.5 within the biogas, threatening ecological and human health. Therein, recycling waste NH3 from the biogas as a raw material of nitrogen fertilizer was tested by optimizing polyester as a sorbent material. After homogeneous catalysis, the converted polyester significantly increased the NH3 adsorption sites within polyester nanopores; correspondingly, the NH3 adsorption capacity increased from 0.56 mg·g-1 to 84.07 mg·g-1. Based on the structural characterization of polyesters, functional groups analysis before and after adsorption, and kinetic analysis during adsorption, chemical adsorption was identified as the dominant mechanism for NH3 adsorption. Moreover, selective adsorption and the regeneration experiments to optimize polyester indicated that NH3 could be efficiently separated from biogas with good regeneration performance. The results demonstrate the efficacy of recycling waste polyester and NH3 from the biogas.

Efficient Adsorption of Ammonia by Surface-Modified Activated Carbon Fiber Mesh

In view of the characteristics and risks of ammonia, its removal is important for industrial production and environmental safety. In this study, viscose-based activated carbon fiber (ACF) was used as a substrate and chemically modified by nitric acid impregnation to enhance the adsorption capacity of the adsorbent for ammonia. A series of modified ACF-based adsorbents were prepared and characterized using BET, FTIR, XPS, and Boehm titration. Isotherm tests (293.15 K, 303.15 K, 313.15 K) and dynamic adsorption experiments were performed. The characterization results showed that impregnation with low concentrations of nitric acid not only increased the surface acidic functional group content but also increased the specific surface area, while impregnation with high concentrations of nitric acid could be able to decrease the specific surface area. ACF-N-6 significantly increased the surface functional group content without destroying the physical structure of the activated carbon fibers. The experimental results showed that the highest adsorption of ammonia by ACFs was 14.08 mmol-L-1 (ACF-N-6) at 293 K, and the adsorption capacity was increased by 165% compared with that of ACF-raw; by fitting the adsorption isotherm and calculating the equivalent heat of adsorption and thermodynamic parameters using the Langmuir-Freundlich model, the adsorption process could be found to exist simultaneously. Regarding physical adsorption and chemical adsorption, the results of the correlation analysis showed that the ammonia adsorption performance was strongly correlated with the carboxyl group content and positively correlated with the relative humidity (RH) of the inlet gas. This study contributes to the development of an efficient ammonia adsorption system with important applications in industrial production and environmental safety.

A novel micro-sphere activated carbon synthesized from waste cigarette butts for ammonia adsorption

Waste cigarette filters mainly contain hardly degradable cellulose acetate, toxic nicotine, and traces of heavy metals, and therefore cause environmental pollution hazards when discarded. In order to convert cigarette butt waste into a valuable product, this article investigates the preparation of activated carbon from cigarette butts via a two-step process of hydrothermal reaction and a subsequent chemical activation with phosphoric acid as an activator. During hydrothermal reaction, it was found that a process of decarboxylation and dehydration cleavage of acetate occurs, leading to micron fragments and subsequent agglomeration into carbonaceous micro-spheres. The cigarette-butts-derived activated carbon micro-spheres have a high BET surface area of ∼ 1406 m2/g and NH3 adsorption capacity of ∼ 35.9 mg/g. It was revealed that the ammonia adsorption capacity tends to be positively and linearly correlated with the acidic functional group content of the activated carbon surface while negatively with BET surface area.