Cation Disorder in Ferroelectric Ba4M2Nb10O30 (M = Na, K, and Rb) Tetragonal Tungsten Bronzes

The effect of cation size on structure and properties of Ba-based tetragonal tungsten bronzes Ba4M2Nb10O30 (M = Na, K or Rb) and Ba4M2Nb8Ti2O30 (M = Ca or Sr)

The second largest family of oxide ferroelectrics, after perovskites, are the tetragonal tungsten bronzes (TTB) with the general formula A24A12C4B12B28O30. Cation disorder in TTBs is known to occur if the size difference between cations is small, but the impact of cation disorder on structure and properties has not yet been extensively addressed. In this study we investigate the effect of the size of the M cation, including cation disorder, on the crystal structure and dielectric properties in the two series Ba4M2Nb10O30 (BMN, A = Na, K and Rb) and Ba4M2Nb8Ti2O30 (BMNT, M = Ca, Sr). Dense and phase pure ceramics in the two series were prepared by a two-step solid state synthesis route. The crystal structures of the materials were characterized by powder X-ray diffraction combined with Rietveld refinement. A close to linear relation between the in-plane lattice parameter (a) and the size of the M-cation were observed. Ba4M2Nb8Ti2O30 was shown to possess cation disorder on the A-sites in line with previous work on Ba4M2Nb10O30. Thermodynamic calculations from density functional theory also indicated a drive for cation disorder in the three BMN compositions. Non-ambient temperature X-ray diffraction revealed contraction of the in-plane (a) and expansion of the out-of-plane (c) lattice parameters at the ferroelectric phase transition for Ba4M2Nb10O30. The ferroelectric transition temperature acquired by dielectric spectroscopy showed a systematically increasing TC with decreasing size of the M-cation within both compositional series studied. The compositional dependence of TC is discussed with respect to the size of the M-cation, cation disorder and the tetragonality, as well as the Ti-content. The relaxor to ferroelectric properties observed by polarization-electric field hysteresis loops are discussed in relation to the relative size of cations on the on A1 and A2 sites and the Ti-content.

A-Site Cation Disorder in SrxBa1-xNb2O6 (x = 0.25, 0.33, 0.50, 0.61) Studied by High-Resolution Resonant X-ray Powder Diffraction

The dielectric and ferroelectric properties of SrxBa1-xNb2O6 (SBN, 0.2 < x < 0.8) are known to be affected by the Sr fraction and can be further controlled by various quenching schemes. Changes in A-site cation configuration are believed to be linked to these changes in properties. In this work, we study the A-site cation disorder in SBN by the use of high-resolution resonant X-ray powder diffraction. The experimental results show that the larger Ba2+ is found exclusively on the larger A2 site, while Sr2+ is found on both the A1 and A2 sites, with an increasing amount on A2 with an increasing Sr fraction. At elevated temperatures, a small migration of Sr2+ from A1 to A2 is observed for SBN50 and SBN61. Linking this change in occupancies to changes in the average cation size on the A1 and A2 sites allows for rationalization of the property changes observed for quenched samples. Furthermore, SBN25 is shown to deviate from the tetragonal P4bm structure and is found to be orthorhombic with a Cmm2 structure.

Revisiting the structures and phase transitions of Ba2NaNb5O15

The room-temperature and low-temperature structure(s) of Ba2NaNb5O15 (BNN) have been debated since the structure was proposed in the 1960s. This work revisits the structures and phase transitions of BNN, combining high-resolution X-ray and neutron powder diffraction with density functional theory calculations. Temperature-dependent high-resolution X-ray powder diffraction patterns are collected from 4 to 918 K, and sequential batch Rietveld refinement using a symmetry mode approach to describe the structure is used to extract the main structural changes as a function of temperature. The data show that the average structure of BNN is best described by the Ama2 space group, and no other structural phase transitions were observed below the ferroelastic transition. The symmetry mode analysis, combining results from diffraction and density functional theory, shows significant octahedral tilting and corrugations of both the A1 and A2 sites along the c direction. A strong correlation between the spontaneous strain and the octahedral tilting was observed, and a potential connection with emerging microstructure at low temperatures is proposed, all enabled by the symmetry mode approach used in this work.