Protonation of Strained Epoxy Resin under Wet Conditions via First-Principles Calculations Using the H+-Shift Method

Design and Mechanistic Insights into α-Helical p-Terphenyl Guanidines as Potent Small-Molecule Antifreeze Agents

Ice formation is a critical challenge across multiple fields, from industrial applications to biological preservation. Inspired by natural antifreeze proteins, we designed and synthesized a new class of small-molecule antifreezes based on α-helical p-terphenyl scaffolds with guanidine side chains. These p-terphenyl guanidines 1, among the smallest molecules that mimic α-helical structures, exhibit potent ice recrystallization inhibition (IRI) activity, similar to that of existing large α-helical antifreeze compounds. The most effective compound, 1a, with four C1-carbon guanidine moieties, demonstrated a superior IRI activity of 0.46 (1 mg/mL). Using molecular dynamics simulations with density-functional theory and separate pKa calculations, we elucidated the mechanisms underlying their antifreeze properties.

Effect of Condensed Water at an Alumina/Epoxy Resin Interface on Curing Reaction

The adhesion of epoxy adhesives to aluminum materials is an important issue in assembling parts for lightweight mobility. Aluminum surfaces typically possess an oxide layer, which readily adsorbs water. In this study, the aggregation states of water and its effect on the curing reaction were examined by placing a water layer between an amorphous alumina surface and a mixture of epoxy and amine components. This study used molecular dynamics simulations and density functional theory calculations. Before the reaction, water molecules strongly adsorbed onto the alumina surface, aggregating excess water. Some water diffused into the epoxy/amine mixture, accelerating the diffusion of unreacted substances. This led to faster reaction kinetics, particularly in proximity to the alumina surface. The adsorption of water molecules onto the alumina surface and the aggregation of excess water were similarly observed even after the curing process. Subsequently, the interaction between the alumina surface and various functional groups of the epoxy/amine mixture was evaluated before and after the reaction. Epoxy monomers had little interaction with the alumina surface before the reaction, whereas hydroxy groups formed by the ring-opening reaction of epoxy groups exhibited notable interaction. Conversely, sulfonyl and amino groups in amine compounds formed hydrogen bonds with OH groups on the alumina surface before the reaction. However, after the reaction, amino groups weakened their interaction with the alumina OH groups as they transformed from primary to tertiary during the curing reaction. Both epoxy and amine monomers/fragments similarly interacted with water molecules, both before and after the reaction. The insights gained from this study are expected to contribute to a better understanding of the impact of moisture absorption on the application of epoxy resins.

Elucidating the Effects of Chemisorbed Water Molecules on the Adhesive Interactions of Epoxy Resin to γ-Alumina Surfaces

The adhesion mechanism of epoxy resin to the γ-alumina (110) surface was investigated using first-principles density functional theory (DFT). Aluminum materials are lightweight and are used in a wide range of industrial fields. Its surface is oxidized to alumina, and the stable surface is known as the γ-alumina (110) surface. The coverage of hydroxy groups by chemisorbed water molecules on this surface varied depending on the pretreatment temperature. In this study, we investigated the adhesive interactions of epoxy resin on four alumina surfaces with different densities of surface hydroxy groups (0, 3, 6, and 9 OH/nm2) and have discussed their effects. At each interface, the energy curves of the vertically displaced epoxy resin were calculated and the adhesive forces were estimated by differentiating these curves. As the coverage of the surface hydroxy groups increased from 0 to 6 OH/nm2, the adhesive strength gradually decreased. However, the adhesive strength at 9 OH/nm2 was relatively large and almost equal to that at 3 OH/nm2. This inverse volcano-type behavior was analyzed via the decomposition of adhesive forces and the crystal orbital Hamilton population (COHP). The decomposition of adhesive forces into DFT and dispersion components revealed that the inverse volcano-type behavior is derived from the DFT component, and the interfacial interactions owing to the DFT component are accompanied by charge transfer. These were investigated using a COHP analysis, which revealed that this behavior was caused by changes in the activity of the aluminum atoms on the surface and surface reconstruction by chemisorbed water molecules. It is noteworthy that the adhesive strength for 9 OH/nm2 was only 6.9% lower than that for 0 OH/nm2 wherein the chemisorbed water molecules were completely removed from the surface. These results are expected to provide a guideline for the adhesion of epoxy resin to aluminum materials.