Charge Carrier Dynamics in Colloidally Synthesized Monolayer MoX2 Nanosheets

Thickness-dependent electronic relaxation dynamics in solution-phase redox-exfoliated MoS2 heterostructures

Electronic relaxation dynamics of solution-phase redox-exfoliated molybdenum disulfide (MoS2) monolayer and multilayer ensembles are described. MoS2 was exfoliated using polyoxometalate (POM) reductants. This process yields a colloidal heterostructure consisting of MoS2 2D sheet multilayers with surface-bound POM complexes. Using two-dimensional electronic spectroscopy, transient bleaching and photoinduced absorption signals were detected at excitation/detection energies of 1.82/1.87 and 1.82/1.80 eV, respectively. Approximate 100-fs bandgap renormalization (BGR) and subsequent defect- and phonon-mediated relaxation on the picosecond timescale were resolved for several MoS2 thicknesses spanning from 1 to 2 L to ∼20 L. BGR rates were independent of sample thickness and slightly slower than observations for chemical vapor deposition-grown MoS2 monolayers. However, defect-mediated relaxation accelerated ∼10-fold with increased sample thicknesses. The relaxation rates increased from 0.33 ± 0.05 to 1.2 ± 0.1 and 3.1 ± 0.4 ps-1 for 1-2 L, 3-4 L, and 20 L fractions. The thicknesses-dependent relaxation rates for POM-MoS2 heterostructures were modeled using a saturating exponential function that showed saturation at thirteen MoS2 layers. The results suggest that the increased POM surface coverage leads to larger defect density in the POM-MoS2 heterostructure. These are the first descriptions of the influence of sample thickness on electronic relaxation rates in solution-phase redox-exfoliated POM-MoS2 heterostructures. Outcomes of this work are expected to impact the development of solution-phase exfoliation of 2D metal-chalcogenide heterostructures.

The Dynamic Interaction of Surfactants with Colloidal Molybdenum Disulfide Nanosheets Calls for Thermodynamic Stabilization by Solvents

Top-down liquid-phase exfoliation (LPE) and bottom-up hot-injection synthesis are scalable methods to produce colloids of two-dimensional (2D) van der Waals (vdW) solids. Generally thought off as two entirely different fields, we show that similar stabilization mechanisms apply to colloids of molybdenum disulfide (MoS₂) produced by both methods. By screening the colloidal stability of MoS₂ produced in a hot-injection synthesis in a wide range of solvents, we observe that colloidal stability can be understood based on solution thermodynamics, wherein matching the solubility parameter of solvent and nanomaterial maximizes colloidal stability. Identical to MoS₂ produced through LPE, optimal solvents to disperse MoS₂ produced from the bottom-up have similar solubility parameters of ≈22 MPa^1/2 and include aromatic solvents with polar functionalities, such as o-dichlorobenzene, and polar aprotic solvents, such as N,N-dimethylformamide. We further complemented our findings by nuclear magnetic resonance (NMR) spectrscopy, highlighting that organic surfactants, such as oleylamine and oleic acid, have a minimal affinity toward the nanocrystal surface and engage in a highly dynamic adsorption/desorption equilibrium. We thus conclude that hot injection yields MoS₂ colloids with comparable surfaces as those produced by LPE. These similarities might offer the prospect of using established procedures developed for LPE nanomaterials to postprocess colloidally synthesized dispersions of 2D colloids as processable inks.