Synthesis of Zinc Blende-Phased CdSe Nanocrystals with Size-Tunable Optical Properties and Adjustable Valence Band Positions

Growth of Size-Tunable Ag2O Polyhedra and Revelation of Their Bulk and Surface Lattices

By primarily adjusting the reagent amounts, particularly the volume of AgNO3 solution introduced, Ag2O cubes with decreasing sizes from 440 to 79 nm, octahedra from 714 to 106 nm, and rhombic dodecahedra from 644 to 168 nm are synthesized. 733 nm cuboctahedra are also prepared for structural analysis. With in-house X-ray diffraction (XRD) peak calibration, shape-related peak shifts are recognizable. Synchrotron XRD measurements at 100 K reveal the presence of bulk and surface layer lattices. Bulk cell constants also deviate slightly. They show a negative thermal expansion behavior with shrinking cell constants at higher temperatures. The Ag2O crystals exhibit size- and facet-dependent optical properties. Bandgaps red-shift continuously with increasing particle sizes. Optical facet effect is also observable. Moreover, synchrotron XRD peaks of a mixture of Cu2O rhombicuboctahedra and edge- and corner-truncated cubes exposing all three crystal faces can be deconvoluted into three components with the bulk and the [111] microstrain phase as the major component. Interestingly, while the unheated Cu2O sample shows clear diffraction peak asymmetry, annealing the sample to 450 K yields nearly symmetric peaks even when returning the sample to room temperature, meaning even moderately high temperatures can permanently change the crystal lattice.

Interfacial Nucleation Mechanism of Water-Soluble Ag-In-S Quantum Dots at Room Temperature and Their Visible Light Catalytic Performance

A novel interfacial reaction nucleation mechanism for the preparation of water-soluble Ag-In-S quantum dots (AIS QDs) was proposed in which interfacial acid regulates the concentration of hydroxide ions outside the complex and sulfur sources attack cations at the interface of the complex, covalent bonds between cations and sulfur sources are formed at the interface of the complex, and the nucleation and growth of crystals is finished at room temperature. By bypassing the heating process normally necessary for crystal nucleation and growth, AIS QDs can be produced on a large scale under simple, mild conditions. At the same time, the characteristics of this mechanism enable AIS QDs to be directly synthesized in an organic pollutant solution. This study represents a significant advance in the mechanism of crystal synthesis and contributes to the photocatalytic decomposition of organic pollutants from theory to practice.