Design of a Bioinert Interface Using an Amphiphilic Block Copolymer Containing a Bottlebrush Unit of Oligo(oxazoline)

Crystalline lamellar films with honeycomb structure from comb-like polymers of poly(2-long-alkyl-2-oxazoline)s

Comb-like copolymers are usually structured by grafting polymeric side chains onto main polymer chain. There are few reports of comb-on-comb polymers in which dense secondary side chains are grafted onto primary side chain. In this work, we synthesized comb polymers with grafted-on-graft side chains (c-PEI-g-Acyl) via an effective acylation reaction of comb polymers possessing polyethyleneimine (PEI) side chain with long-alkyl acyl chlorides. For comparison, we also synthesized homopolymers l-PEI-g-Acyls via reaction of linear PEI with long-alkyl acyl chlorides. Then, we investigated their crystalline feature in the film formation by XRD, DSC and SEM, and found that the polymers tend to form hexagonal lamella structures with bilayer alkyl spacing. The comb polymers c-PEI-g-Acyls and linear polymers l-PEI-g-Acyls were used in preparation of honeycomb film by the "breath-figure" process by dropping chloroform solution of the polymers on substrate. Different to many honeycomb polymeric films which are supported by amorphous phase, interestingly, our polymers easily afford honeycomb films which are supported by crystalline lamellae frames under higher humidity condition. It was found that the comb polymers of c-PEI-g-Acyls with longer PEI primary side chain and long alkyl secondary side chain have advantages in producing honeycomb film than linear polymers of l-PEI-g-Acys.

Modification of a Polymer Surface by Partial Swelling Using Nonsolvents

Surface modification without changing the physical properties in the bulk is of pivotal importance for the development of polymers as devices. We recently proposed a simple surface functionalization method for polymer films by partial swelling using a nonsolvent and demonstrated the incorporation of poly(2-methoxyethyl acrylate) (PMEA), which has an excellent antibiofouling ability, only into the outermost region of a poly(methyl methacrylate) (PMMA) film. We here extend this technology to another versatile polymer, polystyrene (PS). In this case, PS and PMEA have different solubility parameters making it difficult to select a suitable solvent, which is a nonsolvent for PS and a good solvent for PMEA, unlike the combination of PMMA with PMEA. Thus, such a solvent was first sought by examining the swelling behavior of PS films in contact with various alcohols. Once a mixed solvent of methanol/1-butanol (50/50 (v/v)) was chosen, PMEA chains could be successfully incorporated at the outermost region of the PS film. Atomic force microscopy in conjunction with neutron reflectivity revealed that chains of PMEA incorporated in the PS surface region were well swollen in water. This leads to an excellent ability to suppress the adhesion of platelets on the PS film.