Fabrication of Radio-Opaque and Macroporous Injectable Calcium Phosphate Cement

Preferentially Biodegradable Gypsum Fibers Endowing Invisible Microporous Structures and Enhancing Osteogenic Capability of Calcium Phosphate Cements

It is known that hydroxyapatite-type calcium phosphate cement (CPC) shows appreciable self-curing properties, but the phase transformation products often lead to slow biodegradation and disappointing osteogenic responses. Herein, we developed an innovative strategy to endow invisible micropore networks, which could tune the microstructures and biodegradation of α-tricalcium phosphate (α-TCP)-based CPC by gypsum fibers, and the osteogenic capability of the composite cements could be enhanced in vivo. The gypsum fibers were prepared via extruding the gypsum powder/carboxylated chitosan (CC) slurry through a 22G nozzle (410 μm in diameter) and collecting with a calcium salt solution. Then, the CPCs were prepared by mixing the α-TCP powder with gypsum fibers (0-24 wt %) and an aqueous solution to form self-curing cements. The physicochemical characterizations showed that injectability was decreased with an increase in the fiber contents. The μCT reconstruction demonstrated that the gypsum fiber could be distributed in the CPC substrate and produce long-range micropore architectures. In particular, incorporation of gypsum fibers would tune the ion release, produce tunnel-like pore networks in vitro, and promote new bone tissue regeneration in rabbit femoral bone defects in vivo. Appropriate gypsum fibers (16 and 24 wt %) could enhance bone defect repair and cement biodegradation. These results demonstrate that the highly biodegradable cement fibers could mediate the microstructures of conventional CPC biomaterials, and such a bicomponent composite strategy may be beneficial for expanding clinical CPC-based applications.

Characterization of rat vertebrae cortical bone microstructures using confocal Raman microscopy combined to tomography and electron microscopy

BACKGROUND

The rat vertebrae is a good model to study bone regeneration after implantation of biomaterials used to treat bone loss, a major problem in oral and dental surgery. However, the precise characterization of bone microstructures in the rat vertebrae has not been reported. Therefore, the aim of this study was to achieve the complete analysis of such bone, at different scales, in order to have a clear model of healthy bone for comparison with regenerated bone.

METHODS

In order to image the cortical bone of rat caudal vertebra, confocal Raman microscopy was combined with high resolution X-ray micro computed tomography (micro-CT), with scanning electron microscopy (SEM) using backscatter electron imaging and with more conventional histology coloration techniques. SEM and Raman microscopy were done in various regions of the cortical bone corresponding to external, middle and internal areas. The spongy bone was imaged in parallel. Micro-CT was performed on the whole vertebra to monitor the network of haversian canals in the cortical bone. Osteonic canals characteristics, and relative chemical composition were analysed in several regions of interest, in cortical and spongy bone. Five rats were included in this study.

RESULTS

On micro-CT images, differences in intensity were observed in the cortical bone, substantiated by SEM. Chemical analysis with Raman spectra confirmed the difference in composition between the different regions of the cortical and spongy bone. PCA and k-mean cluster analysis separated these groups, except for the external and middle cortical bone. Peak intensity ratio confirmed these results with a CO3 to ν2 PO4 ratio significantly different for the internal cortical bone. Grayscale images stack extracted from micro-CT showed that global architecture of cortical bone was characterized by a dense and complex network of haversian osteonic canals, starting from the surface towards the vertebrae center. The mean diameter of the canals was 18.4 µm (SD 8.6 µm) and the mean length was 450 µm (SD 152 µm). Finally, Raman reconstructed images of the lamellar bone showed an enlargement of the lamellar layer width, both in circumferential lamellar bone and around haversian canals.

CONCLUSIONS

Micro-CT and confocal Raman microscopy are good tools to complete classical analysis using optical and electron microscopy. The results and measurements presented in a rat model known for its small inter-individual differences provide the main characteristics of a mature bone. This study will allow the community working on this rat vertebrate model to have a set of characteristics, in particular on the structure of the haversian canals.