Enhancing the Capacity and Stability of a Tungsten Disulfide Anode in a Lithium-Ion Battery Using Excess Sulfur

Construction of WS2/NC@C nanoflake composites as performance-enhanced anodes for sodium-ion batteries

The development of layered metal sulfides with stable structure and accessible active sites is of great importance for sodium-ion batteries (SIBs). Herein, a simple liquid-mixing method is elaborately designed to immobilize WS2 nanoflakes on N-doped carbon (NC), then further coat carbon to produce WS2/NC@C. In the formation process of this composite, the presence of NC not only avoids the overlap and improves the dispersion of WS2 nanoflakes, but also creates a connection network for charge transfer, where the wrapped carbon provides a stable chemical and electrochemical reaction interface. Thus, the composite of WS2/NC@C exhibits the desired Na+ storage capacity as anticipated. The reversible capacity reaches the high value of 369.8 mA h g-1 at 0.2 A g-1 after 200 cycles, while excellent rate performances and cycle life are also acquired in that capacity values of 256.7 and 219.6 mA h g-1 at 1 and 5 A g-1 are preserved after 1000 cycles, respectively. In addition, the assembled sodium-ion hybrid capacitors (SIHCs, AC//WS2/NC@C) exhibit an energy/power density of 68 W h kg-1 at 64 W kg-1, and capacity retention of 82.9% at 1 A g-1 after 2000 cycles. The study provides insight into developing layered metal sulfides with eminent performance of Na+ storage.

Low volume expansion hierarchical porous sulfur-doped Fe2O3@C with high-rate capability for superior lithium storage

Ingenious morphology design and doping engineering have remarkable effects on enhancing conductivity and reducing volume expansion, which need to be improved by transition metal oxides serving as anode materials for lithium-ion batteries. Herein, S_0.15-Fe₂O₃@C nano-spindles with a hierarchical porous structure are obtained by carbonizing MIL-88B@PDA and subsequent high-temperature S-doping. Kinetic analysis showed that S-doping increases capacitive contribution, enhances charge transfer capability and accelerates Li⁺ diffusion rate. Therefore, the S_0.15-Fe₂O₃@C electrode exhibits superior lithium storage performance with a remarkable specific capacity of 1014.4 mA h g^-1 at 200 mA g^-1, ultrahigh rate capability of 513.1 mA h g^-1 at 5.0 A g^-1, and excellent cycling stability of 842.3 mA h g^-1 at 1.0 A g^-1 after 500 cycles. Moreover, the size of S_0.15-Fe₂O₃@C particles barely changed after 50 cycles, indicating an extremely low volume expansion, related to the carbon shell, fine Fe₂O₃ nanoparticles, abundant voids inside, and improved kinetics. This strategy can be applied to other metal oxides for synthesizing anodes with high-rate capability and low volume expansion.