Ionic Liquid-Induced Multisite Synergistic Interactions for Highly Efficient Inverted Perovskite Solar Cells

Anion Binding Interaction Enhances the Robustness of Iodide for High-Performance Perovskite Solar Cells

Owing to the ionic bond nature of the Pb-I bond, the iodide at the interface of perovskite polycrystalline films was easily lost during the preparation process, resulting in the formation of a large number of iodine vacancy defects. The presence of iodine vacancy defects can cause nonradiative recombination, provide a pathway for iodide migration, and be harmful to the power conversion efficiency (PCE) and stability of organic-inorganic hybrid perovskite solar cells (HPSCs). Here, in order to increase the robustness of iodides at the interface, a strategy to introduce anion binding effects was developed to stabilize the perovskite films. It was demonstrated that the N,N'-diphenylurea (DPU), characterized by high anionic binding constants and a Y-shaped structure, provides a relatively strong hydrogen bond donor site to effectively reduce the iodine loss during film preparation and inhibits iodide migration in the device working condition. As expected, the reduced iodine loss considerably improves the quality of the perovskite films and suppresses nonradiative recombination. The performance of the device after DPU modification was significantly increased, with the PCE rising from 23.65 to 25.01% with huge stability enhancement as well.

Co-Self-Assembled Monolayers Modified NiOx for Stable Inverted Perovskite Solar Cells

[4-(3,6-dimethyl-9H-carbazol-9yl)butyl]phosphonic acid (Me-4PACz) self-assembled molecules (SAM) are an effective method to solve the problem of the buried interface of NiOx in inverted perovskite solar cells (PSCs). However, the Me-4PACz end group (carbazole core) cannot forcefully passivate defects at the bottom of the perovskite film. Here, a Co-SAM strategy is employed to modify the buried interface of PSCs. Me-4PACz is doped with phosphorylcholine chloride (PC) to form a Co-SAM to improve the monolayer coverage and reduce leakage current. The phosphate group and chloride ions (Cl-) in PC can inhibit NiOx surface defects. Meantime, the quaternary ammonium ions and Cl- in PC can fill organic cations and halogen vacancies in the perovskite film to enable defects passivation. Moreover, Co-SAM can promote the growth of perovskite crystals, collaboratively solve the problem of buried defects, suppress nonradiative recombination, accelerate carrier transmission, and relieve the residual stress of the perovskite film. Consequently, the Co-SAM modified devices show power conversion efficiencies as high as 25.09% as well as excellent device stability with 93% initial efficiency after 1000 h of operation under one-sun illumination. This work demonstrates the novel approach for enhancing the performance and stability of PSCs by modifying Co-SAM on NiOx.

Healing the Buried Interface by a Plant-Derived Green Passivator for Carbon-Based CsPbIBr2 Perovskite Solar Cells

Perovskite solar cells (PSCs) have attracted extensive attention in photovoltaic applications owing to their superior efficiency, and the buried interface plays a significant role in determining the efficiency and stability of PSCs. Herein, a plant-derived small molecule, ergothioneine (ET), is adopted to heal the defective buried interface of CsPbIBr2-based PSC to improve power conversion efficiency (PCE). Because of the strong interaction between Lewis base groups (-C═O and -C═S) in ET and uncoordinated Pb2+ in the perovskite film from the theoretical simulations and experimental results, the defect density of the CsPbIBr2 perovskite film is significantly reduced, and therefore, the nonradiative recombination in the corresponding device is simultaneously suppressed. Consequently, the target device achieves a high PCE of 11.13% with an open-circuit voltage (VOC) of 1.325 V for hole-free, carbon-based CsPbIBr2 PSCs and 14.56% with a VOC of 1.308 V for CsPbI2Br PSCs. Furthermore, because of the increased ion migration energy, the detrimental phase segregation in this mixed-halide perovskite is weakened, delivering excellent long-term stability for the unencapsulated device in ambient conditions over 70 days with a 96% retention rate of initial efficiency.