Enhancing the Cell-Biological Performances of Hydroxyapatite Bioceramic by Constructing Silicate-Containing Grain Boundary Phases via Sol Infiltration

Improvement in mechanical strength and biological function of 3D-printed trimagnesium phosphate bioceramic scaffolds by incorporating strontium orthosilicate

Trimagnesium phosphate (TMP) bioceramic scaffolds are deemed as promising bone grafts, but their mechanical and biological properties are yet to be improved. In the study, strontium orthosilicate (SrOS) was used to modify the TMP scaffolds, whose macroporous structure was constructed by the filament deposition-type 3D printing method. The new phases of SrMg2(PO4)2 and Sr2MgSi2O7, which showed nanocrystalline topography, were produced in the 3D-printed TMP/SrOS bioceramic composite scaffolds. The compressive strength (1.8-64.1 MPa) and porosity (39.7%-71.4%) of the TMP/SrOS scaffolds could be readily tailored by changing the amounts of SrOS additives and the sintering temperature. The TMP/SrOS scaffolds gradually degraded in the aqueous solution, consequently releasing ions of magnesium, strontium and silicon. In contrast with the TMP scaffolds, the TMP/SrOS bioceramic scaffolds had profoundly higher compressive strength, and enhanced cell proliferative and osteogenic activities. The TMP/SrOS scaffolds incorporated with 5 wt% SrOS had the highest mechanical strength and beneficial cellular function, which made them promising for treating different sites of bone defects.

Realizing Both Antibacterial Activity and Cytocompatibility in Silicocarnotite Bioceramic via Germanium Incorporation

The treatment of infective or potentially infectious bone defects is a critical problem in the orthopedic clinic. Since bacterial activity and cytocompatibility are always contrary factors, it is hard to have them both in one material. The development of bioactive materials with a good bacterial character and without sacrificing biocompatibility and osteogenic activity, is an interesting and valuable research topic. In the present work, the antimicrobial characteristic of germanium, GeO2 was used to enhance the antibacterial properties of silicocarnotite (Ca5(PO4)2SiO4, CPS). In addition, its cytocompatibility was also investigated. The results demonstrated that Ge–CPS can effectively inhibit the proliferation of both Escherichia coli (E. coli) and Staphylococcus aureus (S. aureus), and it showed no cytotoxicity to rat bone marrow-derived mesenchymal stem cells (rBMSCs). In addition, as the bioceramic degraded, a sustainable release of germanium could be achieved, ensuring long-term antibacterial activity. The results indicated that Ge–CPS has excellent antibacterial activity compared with pure CPS, while no obvious cytotoxicity was observed, which could make it a promising candidate for the bone repair of infected bone defects.