Can Plasmonic Effect Cause an Increase in the Catalytic Reduction of p-nitrophenol by Sodium Borohydride over Au Nanorods?

Bottom-Up Then Top-Down Synthesis of Gold Nanostructures Using Mesoporous Silica-Coated Gold Nanorods

Gold nanostructures were synthesized by etching away gold from heat-treated mesoporous silica-coated gold nanorods (AuNR@mSiO2), providing an example of top-down modification of nanostructures made using bottom-up methodology. Twelve different types of nanostructures were made using this bottom-up-then-top-down synthesis (BUTTONS), of which the etching of the same starting nanomaterial of AuNR@mSiO2 was found to be controlled by how AuNR@mSiO2 were heat treated, the etchant concentration, and etching time. When the heat treatment occurred in smooth moving solutions in round-bottomed flasks, red-shifted longitudinal surface plasmon resonance (LSPR) was observed, on the order of 10-30 min, indicating increased aspect ratios of the gold nanostructures inside the mesoporous silica shells. When the heat treatment occurred in turbulent solutions in scintillation vials, a blue shift of the LSPR was obtained within a few minutes or less, resulting from reduced aspect ratios of the rods in the shells. The influence of the shape of the glassware, which may impact the flow patterns of the solution, on the heat treatment was investigated. One possible explanation is that the flow patterns affect the location of opened pores in the mesoporous shells, with the smooth flow of solution mainly removing CTAB surfactants from the pores along the cylindrical body of mSiO2, therefore increasing the aspect ratios after etching, and the turbulent solutions removing more surfactants from the pores of the two ends or tips of the silica shells, hence decreasing the aspect ratios after etching. These new stable gold nanostructures in silica shells, bare and without surfactant protection, may possess unique chemical properties and capabilities. Catalysis using heat-treated nanomaterials was studied as an example of potential applications of these nanostructures.

Preparing Alumina-Supported Gold Nanowires for Alcohol Oxidation

The development of shape-controlled noble metal nanocrystals such as nanowires (NWs) is progressing steadily owing to their potentially novel catalytic properties and the ease with which they can be prepared by reducing the metal ions in a particular solution as capping agents. Recently, many reports have been presented on the preparation of shape-controlled Au nanocrystals, such as nanostars and nanoflowers, by a one-pot method using 2-[4-(2-hydroxyethyl)-1-piperazinyl] ethanesulfonic acid (HEPES) as capping and reducing agents. The catalytic activity is depressed due to the adsorption of the capping agent onto a Au surface. Since HEPES has low binding affinities on the Au surface, shape-controlled nanocrystals obtained using HEPES are effective for application as nanocatalysts because HEPES was easily removed from the Au surface. In this study, we report the preparation of AuNWs, with an average diameter of 7.7 nm and lengths of a few hundred nanometers, in an aqueous solution containing HEPES and sodium borohydride. A γ-Al2O3-supported AuNW (AuNW/γ-Al2O3) catalyst was obtained using catalytic supporters and a water extraction method that removed HEPES from the Au surface without morphological changes. AuNW/γ-Al2O3 was then utilized to catalyze the oxidation of 1-phenylethyl alcohol to acetophenone. The formation rate of acetophenone over AuNW/γ-Al2O3 was 3.2 times that over γ-Al2O3-supported spherical Au nanoparticles (AuNP/γ-Al2O3) with almost the same diameter.