Enhanced Cycle Stability of Crumpled Graphene-Encapsulated Silicon Anodes via Polydopamine Sealing

Encapsulating a Responsive Hydrogel Core for Void Space Modulation in High-Stability Graphene-Wrapped Silicon Anodes

Due to its formidably high theoretical capacity (3590 mAh/g at room temperature), silicon (Si) is expected to replace graphite as the dominant anode for higher energy density lithium (Li)-ion batteries. However, stability issues stemming from silicon's significant volume expansion (∼300%) upon lithiation have slowed down commercialization. Herein, we report the design of a scalable process to engineer core-shell structures capable of buffering this volume expansion, which utilize a core made up of a poly(ethylene oxide)-carboxymethyl cellulose hydrogel and silicon protected by a crumpled graphene shell. The volume expansion of the hydrogel upon exposure to water creates a void space between the Si-Si and Si-rGO interfaces within the core when the gel dries. Unlike sacrificial spacers, the dehydrated hydrogel remains in the core and acts as an elastic Li-ion conductor, which improves the stability and high rate performance. The optimized composite electrodes retain ∼81.7% of their initial capacity (1055 mAh/(g_rGO+gel+Si)) after 320 cycles when an active material loading of 1 mg/cm² is used. At more practical mass loadings (2.5 mg/cm²), the electrodes achieve 2.04 mAh/cm² and retain 79% of this capacity after 200 cycles against a lithium half-cell. Full cells assembled using a lithium ion phosphate cathode lose only 6.7% of their initial capacity over 100 cycles, demonstrating the potential of this nanocomposite anode for use in next-generation Li-ion batteries.

Controlling Void Space in Crumpled Graphene-Encapsulated Silicon Anodes using Sacrificial Polystyrene Nanoparticles

Silicon anodes have a theoretical capacity of 3590 mAh g^-1 (for Li₁₅ Si₄ , at room temperature), which is tenfold higher than the graphite anodes used in current Li-ion batteries. This, and silicon's natural abundance, makes it one of the most promising materials for next-generation batteries. Encapsulating silicon nanoparticles (Si NPs) in a crumpled graphene shell by spray drying or spray pyrolysis are promising and scalable methods to produce core-shell structures, which buffer the extreme volume change (>300 vol %) caused by (de)lithiaton of silicon. However, capillary forces cause the graphene-based materials to tightly wrap around Si NP clusters, and there is little control over the void space required to further improve cycle life. Herein, a simple strategy is developed to engineer void-space within the core by incorporating varying amounts of similarly sized polystyrene (PS) nanospheres in the spray drier feed mixture. The PS completely decomposes during thermal reduction of the graphene oxide shell and results in Si cores of varying porosity. The best performance is achieved at a 1 : 1 ratio (PS/Si), leading to high capacities of 1638, 1468, and 1179 mAh g^-1 _Si+rGO at 0.1, 1, and 4 A g^-1 , respectively. Moreover, at 1 A g^-1 , the capacity retention is 80.6 % after 200 cycles. At a practical active material loading of 2.4 mg cm^-2 , the electrodes achieve an areal capacity of 2.26 mAh cm^-2 at 1 A g^-1 .