Abdellatif M, Nomura K. Synthesis of Polyesters Containing Long Aliphatic Methylene Units by ADMET Polymerization and Synthesis of ABA-Triblock Copolymers by One-Pot End Modification and Subsequent Living Ring-Opening Polymerization. ACS OMEGA 2024; 9:9109-9122. [PMID: 38434832 PMCID: PMC10906047 DOI: 10.1021/acsomega.3c07858] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Download PDF] [Figures] [Subscribe] [Scholar Register] [Received: 10/09/2023] [Revised: 01/25/2024] [Accepted: 02/05/2024] [Indexed: 03/05/2024]
Abstract
The synthesis of high-molecular-weight (Mn up to 62,000 g/mol) polyesters has been achieved by acyclic diene metathesis (ADMET) polymerization of α,ω-dienes prepared from biobased bis(undec-10-enoate) and diols [ethylene glycol (M1), propylene glycol (M2), 1,9-nonanediol (M3), 1,4-benzenedimethanol (M4), and hydroquinone (M5)] using ruthenium-carbene catalysts. Replacement of the solvent during the ADMET polymerization was effective for obtainment of the high-molecular-weight polymers (expressed as P1-P5). The melting temperatures (Tm) in the resultant polyesters were dependent upon the diol (middle) segment employed, and the polymer prepared from M5 exceeded 100 °C (a Tm value of 122.5 °C). The polymerization of M3 and M4 in the presence of 1,4-cis-diacetoxy-2-butene (DAB, as the chain transfer agent) afforded the telechelic polyesters [P3(OAc)2 and P4(OAc)2, respectively] containing acetoxy end groups exclusively. The resultant polymers containing hydroxy group termini [P3(OH)2 and P4(OH)2], prepared by the selective deprotection of the acetoxy end groups, were treated with AlEt3 followed by addition of ε-caprolactone to afford the ABA-type triblock copolymers exclusively, through a living ring-opening polymerization. The depolymerization (hydrolysis) under basic conditions (NaOH aqueous solution) of P3 was explored.
Collapse
Affiliation(s)
- Mohamed
Mehawed Abdellatif
- Department
of Chemistry, Graduate School of Science, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan
- Chemistry
of Tanning Materials and Leather Technology Department, Chemical Industries Research Institute, National Research
Centre, 33 El Buhouth
St., Dokki, Giza BP 12622, Egypt
| | - Kotohiro Nomura
- Department
of Chemistry, Graduate School of Science, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan
| |
Collapse
|
2
|
Go LOP, Abdellatif MM, Makino R, Shimoyama D, Higashi S, Hirano H, Nomura K. Synthesis of Network Biobased Aliphatic Polyesters Exhibiting Better Tensile Properties than the Linear Polymers by ADMET Polymerization in the Presence of Glycerol Tris(undec-10-enoate). Polymers (Basel) 2024; 16:468. [PMID: 38399846 PMCID: PMC10891964 DOI: 10.3390/polym16040468] [Citation(s) in RCA: 0] [Impact Index Per Article: 0] [Reference Citation Analysis] [Abstract] [Key Words] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 12/30/2023] [Revised: 01/27/2024] [Accepted: 02/05/2024] [Indexed: 02/25/2024] Open
Abstract
Development of biobased aliphatic polyesters with better mechanical (tensile) properties in film has attracted considerable attention. This report presents the synthesis of soluble network biobased aliphatic polyesters by acyclic diene metathesis (ADMET) polymerization of bis(undec-10-enyl)isosorbide diester [M1, dianhydro-D-glucityl bis(undec-10-enoate)] in the presence of a tri-arm crosslinker [CL, glycerol tris(undec-10-enoate)] using a ruthenium-carbene catalyst, and subsequent olefin hydrogenation using RhCl(PPh3)3. The resultant polymers, after hydrogenation (expressed as HCP1) and prepared in the presence of 1.0 mol% CL, showed better tensile properties than the linear polymer (HP1) with similar molecular weight [tensile strength (elongation at break): 20.8 MPa (282%) in HP1 vs. 35.4 MPa (572%) in HCP1]. It turned out that the polymer films prepared by the addition of CL during the polymerization (expressed as a 2-step approach) showed better tensile properties. The resultant polymer film also shows better tensile properties than the conventional polyolefins such as linear high density polyethylene, polypropylene, and low density polyethylene.
Collapse
Affiliation(s)
- Lance O’Hari P. Go
- Department of Chemistry, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan; (L.O.P.G.); (M.M.A.)
| | - Mohamed Mehawed Abdellatif
- Department of Chemistry, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan; (L.O.P.G.); (M.M.A.)
| | - Ryoji Makino
- Department of Chemistry, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan; (L.O.P.G.); (M.M.A.)
| | - Daisuke Shimoyama
- Department of Chemistry, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan; (L.O.P.G.); (M.M.A.)
| | - Seiji Higashi
- Osaka Research Institute of Industrial Science and Technology (ORIST), 1-6-50, Morinomiya, Joto-ku, Osaka 536-8553, Japan; (S.H.)
| | - Hiroshi Hirano
- Osaka Research Institute of Industrial Science and Technology (ORIST), 1-6-50, Morinomiya, Joto-ku, Osaka 536-8553, Japan; (S.H.)
| | - Kotohiro Nomura
- Department of Chemistry, Tokyo Metropolitan University, 1-1 Minami Osawa, Hachioji, Tokyo 192-0397, Japan; (L.O.P.G.); (M.M.A.)
| |
Collapse
|
3
|
Kojima M, Wang X, Go LO, Makino R, Matsumoto Y, Shimoyama D, Abdellatif MM, Kadota J, Higashi S, Hirano H, Nomura K. Synthesis of High Molecular Weight Biobased Aliphatic Polyesters Exhibiting Tensile Properties Beyond Polyethylene. ACS Macro Lett 2023; 12:1403-1408. [PMID: 37793171 PMCID: PMC10586459 DOI: 10.1021/acsmacrolett.3c00481] [Citation(s) in RCA: 2] [Impact Index Per Article: 2.0] [Reference Citation Analysis] [Abstract] [Grants] [Track Full Text] [Journal Information] [Subscribe] [Scholar Register] [Received: 08/13/2023] [Accepted: 09/13/2023] [Indexed: 10/06/2023]
Abstract
Synthesis of high molecular weight polyesters prepared by acyclic diene metathesis (ADMET) polymerization of bis(undec-10-enoate) with isosorbide (M1), isomannide (M2), and 1,3-propanediol (M3) and the subsequent hydrogenation have been achieved by using a molybdenum-alkylidene catalyst. The resultant polymers (P1) prepared by the ADMET polymerization of M1 (in toluene at 25 °C) possessed high Mn values (Mn = 44400-49400 g/mol), and no significant differences in the Mn values and the PDI (Mw/Mn) values were observed in the samples after the hydrogenation. Both the tensile strength and the elongation at break in the hydrogenated polymers from M1 (HP1) increased upon increasing the molar mass, and the sample with an Mn value of 48200 exhibited better tensile properties (tensile strength of 39.7 MPa, elongation at break of 436%) than conventional polyethylene, polypropylene, as well as polyester containing C18 alkyl chains. The tensile properties were affected by the diol segment employed, whereas HP2 showed a similar property to HP1.
Collapse
Affiliation(s)
- Mika Kojima
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Xiuxiu Wang
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Lance O’Hari
P. Go
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Ryoji Makino
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Yuichi Matsumoto
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Daisuke Shimoyama
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Mohamed Mehawed Abdellatif
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| | - Joji Kadota
- Osaka
Research Institute of Industrial Science and Technology (ORIST), 1-6-50, Morinomiya, Joto-ku, Osaka 536-8553, Japan
| | - Seiji Higashi
- Osaka
Research Institute of Industrial Science and Technology (ORIST), 1-6-50, Morinomiya, Joto-ku, Osaka 536-8553, Japan
| | - Hiroshi Hirano
- Osaka
Research Institute of Industrial Science and Technology (ORIST), 1-6-50, Morinomiya, Joto-ku, Osaka 536-8553, Japan
| | - Kotohiro Nomura
- Department
of Chemistry, Tokyo Metropolitan University, 1-1 minami Osawa, Hachioji, Tokyo 192-0397, Japan
| |
Collapse
|