In Situ Cellulose Nanocrystal-Reinforced Glycerol-Based Biopolyester for Enhancing Poly(lactic acid) Biocomposites

Dispersibility Characterization of Cellulose Nanocrystals in Polymeric-Based Composites

Cellulose nanocrystals (CNCs) are hydrophilic nanoparticles extracted from biomass with properties and functions different from cellulose and are being developed for property-oriented applications such as high stiffness, abundant active groups, and biocompatibility. It has broad application prospects in the field of composite materials, while the dispersibility of the CNC in polymers is the key to its application performance. Many reviews have discussed in-depth the modification strategies to improve the dispersibility of the CNC and summarized all characterization for the CNC, but there are no reviews on the in-depth exploration of dispersion characterization. This review is a comprehensive summary of the characterization of CNC dispersion in the matrix in terms of direct observation, indirect evaluation, and quantified evaluation, summarizing how and why different characterization tools reveal dispersibility. In addition, "decision tree" flowcharts are presented to provide the reader with a reference for selecting the appropriate characterization method for a specific composite.

High-heat and UV-barrier poly(lactic acid) by microwave-assisted functionalization of waste natural fibers

The application of poly(lactic acid) (PLA) in the packaging area is frequently dwarfed by the inadequate gas/water barrier properties, low heat resistance and high UV transmittance. Herein, an environmentally friendly and high-efficiency microwave-assisted functionalization (MAF) approach was proposed to aqueous grafting waste bamboo fibers with the bridging agent. It permitted significant promotion of interfacial interactions between the MAF bamboo fibers (MAFBs) and neighboring PLA chains, contributing to uniform dispersion and intimate interphase. Featuring the morphological features, the MAFB-reinforced (5, 10 and 20 wt%) PLA biocomposites achieved an unexpected combination of high mechanical properties, exceptional resistance to heat deflection and UV irradiation, and excellent water barrier performance. Upon addition of only 5 wt% MAFBs, the tensile strength and toughness of PLA composite films were increased to 46.5 MPa and 0.6 MJ/m³, increasing over 52 % and nearly 107 % compared to those of the counterpart loaded pristine bamboo fibers (PBFs), respectively. This was favorably accompanied by the remarkably reduced water vapor permeability, falling down to the lowest value of 3.5 × 10^-11 g∙m/Pa∙s∙m² for PLA/MAFB (80/20) with a decrease of nearly 79 % compared to the counterpart. It is of interest to note the MAFB-enabled nearly 100 % UV-blocking ratio for PLA loaded 10 and 20 wt% fibers, as well as excellent resistance to heat deflection even at high temperatures like 120 °C. This effort paves the way to multifunctional natural fibers with high affinity to PLA for elegant implementation of high-heat and UV-resistant packaging materials in an ecofriendly manner.

High-Strength, Low-Permeable, and Light-Protective Nanocomposite Films Based on a Hybrid Nanopigment and Biodegradable PLA for Food Packaging Applications

Herein, a multifunctional filler, a dye (organic)-clay (inorganic) hybrid nanopigment (DCNP), was embedded into polylactic acid (PLA) to fabricate a colored biodegradable/biocompatible film, which is explored as a high thermomechanical resistant as well as a superior light and mass transport barrier for food packaging applications. In this respect, the DCNP was synthesized through a wet chemical process with a reaction yield of 76% and incorporated into a PLA matrix at various concentrations using a solution casting method. The morphological characterizations revealed partially intercalated/exfoliated structure for PLA-DCNP films. The samples filled with DCNP showed up to 20% and 12 °C improvements in storage modulus (E') and glass transition temperature (T g), respectively, compared to those with neat PLA. Incorporation of a small amount of DCNP into the PLA matrix significantly declined the water vapor and gas permeability of PLA by 36 and 54%, respectively. The optical property investigations indicated remarkable color characteristics and light protection performance of the samples containing DCNP. The results also showed better performance of the PLA-DCNP film compared to that of the PLA-Cloisite 20A sample at an identical filler loading. In conclusion, the desirable properties of the resulting films highlighted the potential application of such nanocomposite films as a promising option for food packaging materials.