Thermal Stability and Flame Retardancy of a Cured Trifunctional Epoxy Resin with the Synergistic Effects of Silicon/Titanium

The Flame Retardant and Mechanical Properties of the Epoxy Modified by an Efficient DOPO-Based Flame Retardant

Currently, the mechanical performance reduction caused by excessive phosphorus content in the halogen-free flame-retardant EP has been an obstacle to its extensive application. This study presents the effective synthesis of a novel flame-retardant BDD with great efficiency, achieving an optimum phosphorus level of merely 0.25 wt %. The structure of BDD was verified by FTIR, 1H NMR, 31P NMR and XPS spectra. To investigate the flame-retardant properties of BDD, several EPs with various phosphorus levels were synthesized. The addition of phosphorus to the EP significantly increases its LOI value from 25.8% to 33.4% at a phosphorus level of 0.25 wt%. Additionally, the resin achieves a V-0 grade in the UL 94 test. The P-HRR and THR of the modified resin measured by the cone calorimeter are also significantly reduced. At the same time, the addition of a modest quantity of BDD has a minimal impact on the mechanical properties of epoxy resin. This study shows that the removal of hydroxyl groups significantly enhances the fire resistance of phosphate-based flame retardants, thereby providing a novel approach to synthesizing efficient flame retardants.

Synthesis of a Novel Flame Retardant Containing Phosphorus, Nitrogen, and Silicon and Its Application in Epoxy Resin

A novel flame retardant (TDA) containing phosphorus, nitrogen, and silicon was synthesized successfully via a controllable ring-opening addition reaction between 1,3,5-triglycidyl isocyanurate, 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide, and 3-aminopropyltriethoxysilane, and TDA was then blended with diglycidyl ether of bisphenol A to prepare flame-retardant epoxy resins (EPs). The chemical structure and components of TDA were confirmed by Fourier transform infrared (FTIR) spectra, ³¹P nuclear magnetic resonance, and X-ray photoelectron spectroscopy. Thermogravimetric analysis results indicated that after the introduction of TDA, cured EP maintained good thermal stability with a minimum initial decomposition temperature of 337.6 °C, and the char yields of a EP/TDA-5 sample significantly increased by 76.2% compared with that of the neat EP thermoset. Additionally, with the addition of 25.0 wt % TDA (1.05 wt % phosphorus loading), the limited oxygen index value of cured EP increased from 22.5% of pure EP to 33.4%, and vertical burning V-0 rating was easily achieved. Meanwhile, after the incorporation of TDA, the total heat release and total smoke production of the EP/TDA-5 sample obviously reduced by 28.9 and 27.7% in the cone calorimeter test, respectively. Flame-retardant performances and flame-retardant mechanisms were further analyzed by scanning electron microscopy, FTIR, energy-dispersive spectrometry, and pyrolysis gas chromatography/mass spectrometry. The results reveal that the synergistic effect of phosphorus, nitrogen, and silicon plays an excellent flame-retardant role in both gaseous and condensed phases. In addition, the mechanical and dynamic mechanical properties of cured EP thermosets are well maintained rather than destroyed. All the results demonstrate that TDA endows epoxy resin with excellent flame retardancy and possesses great promise in the industrial field.

Flame-Retardant Performance of Epoxy Resin Composites with SiO2 Nanoparticles and Phenethyl-Bridged DOPO Derivative

Flame retardancy of epoxy resin (EP) plays a vital role in its applications. When inorganic nanomaterials form inorganic/organic nanocomposites, they exhibit special flame-retardant effects. In this study, EP nanocomposites were prepared by the incorporation of SiO2 nanoparticles and phenethyl-bridged 9,10-dihydro-9-oxa-10-phosphaphenanthrene-10-oxide (DOPO) derivative (DiDOPO), and the synergistic effects of SiO2 nanoparticles and DiDOPO on the flame-retardant performance of EP were discussed. Results indicated that the introduction of only 15 wt % SiO2 and 5 wt % DiDOPO in EP leads to the increase in the limiting oxygen index from 21.8 to 30.2%, and the nanocomposites achieve the UL-94 V-0 rating. Thermogravimetric analysis revealed that char yield increases with the increase in the SiO2 content of the nanocomposites and that an increased amount of thermally stable carbonaceous char is formed. SiO2 nanoparticles can improve the thermal stability and mechanical performance of EP; hence, the nanoparticles can serve as an efficient adjuvant for the DiDOPO/EP flame-retardant system.