Elasticity through Nanoscale Distortions in Periodic Surfactant-Templated Porous Silica under High Pressure

Synthetic chemistry with periodic mesostructures at high pressure

Over the last two decades, researchers have studied extensively the synthesis of mesostructured materials, which could be useful for drug delivery, catalytic cracking of petroleum, or reinforced plastics, among other applications. However, until very recently researchers used only temperature as a thermodynamic variable for synthesis, completely neglecting pressure. In this Account, we show how pressure can affect the synthetic chemistry of periodic mesoporous structures with desirable effects. In its simplest application, pressure can crystallize the pore walls of periodic mesoporous silicas, which are difficult to crystallize otherwise. The motivation for the synthesis of periodic mesoporous silica materials (with pore sizes from 2 to 50 nm) 20 years ago was to replace the microporous zeolites (which have pore sizes of <2 nm) in petroleum cracking applications, because the larger pore size of mesoporous materials allows for faster transport of larger molecules. However, these mesoporous materials could not replace zeolite materials because they showed lower hydrothermal stability and lower catalytic activity. This reduced performance has been attributed to the amorphous nature of the mesoporous materials' channel walls. To address this problem, we developed the concept of "nanocasting at high pressure". Through this approach, we produced hitherto-unavailable, periodic mesostructured silicas with crystalline pore walls. In nanocasting, we compress a periodic mesostructured composite (e.g. a periodic mesoporous silica with carbon-filled pores) and subsequently heat it to induce the selective crystallization of one of the two phases. We attain the necessary high pressure for synthesis using piston-cylinder and multianvil apparatuses. Using periodic mesostructured silica/carbon nanocomposites as starting material, we have produced periodic mesoporous coesite and periodic mesoporous quartz. The quartz material is highly stable under harsh hydrothermal conditions (800°C in pure steam), verifying that crystallinity in the channel walls of periodic mesoporous silicas increases their hydrothermal stability. Even without including the carbon phase in the silica pores, we could obtain mesoporous coesite materials. We found similar behavior for periodic mesoporous carbons, which convert into transparent, mesoporous, nanopolycrystalline diamond at high-pressure. We also show that periodic mesoporous materials can serve as precursors for nanocrystals of high-pressure phases. We obtained nearly monodisperse, discrete stishovite nanocrystals from periodic mesoporous silicas and coesite nanocrystals from periodic mesoporous organosilicas. The stishovite nanocrystals disperse in water and form colloidal solutions of individual stishovite nanocrystals. The stishovite nanocrystals could be useful for machining, drilling, and polishing. Overall, the results show that periodic mesoporous materials are suitable starting materials for the synthesis of nanoporous high-pressure phases and nanocrystals of high pressure phases. The substantially enhanced hydrothermal stability seen in periodic mesoporous silicas synthesized at high pressure demonstrates that high pressure can be a useful tool to produce porous materials with improved properties. We expect that synthesis using mesostructures at high pressure can be extended to many other materials beyond silicas and carbons. Presumably, this chemistry can also be extended from mesoporous to microporous and macroporous materials.

Catalyst-free synthesis of transparent, mesoporous diamond monoliths from periodic mesoporous carbon CMK-8

We report on the synthesis of optically transparent, mesoporous, monolithic diamond from periodic mesoporous carbon CMK-8 at a pressure of 21 GPa. The phase transformation is already complete at a mild synthesis temperature of 1,300 degrees C without the need of a catalyst. Surprisingly, the diamond is obtained as a mesoporous material despite the extreme pressure. X-ray diffraction, SEM, transmission electron microscopy, selected area electron diffraction, high-resolution transmission electron microscopy, and Z-contrast experiments suggest that the mesoporous diamond is composed of interconnected diamond nanocrystals having diameters around 5-10 nm. The Brunauer Emmett Teller surface area was determined to be 33 m2 g(-1) according Kr sorption data. The mesostructure is diminished yet still detectable when the diamond is produced from CMK-8 at 1,600 degrees C and 21 GPa. The temperature dependence of the porosity indicates that the mesoporous diamond exists metastable and withstands transformation into a dense form at a significant rate due to its high kinetic inertness at the mild synthesis temperature. The findings point toward ultrahard porous materials with potential as mechanically highly stable membranes.

Mechanical heterogeneity in nanoscale films of liquid silica

Molecular dynamics simulations are carried out for slabs of silica liquid with thicknesses between 1 and 3 nm . A local analysis of the Born contribution to the elastic modulus, CB, shows that the elasticity is not uniform throughout the slabs--CB is identical to that of bulk silica in the slab interior, but CB is larger at the slab edges. The larger CB at the slab edges is due to a distinct atomic level structure characterized by larger density, larger concentration of more highly coordinated ions, and smaller silica rings.