Analysis of the Crystal Structure and Optical Spectra of Stoichiometric SmOF

Synthesis, crystal-structure refinement and properties of bastnaesite-type PrF[CO3], SmF[CO3] and EuF[CO3]

By adding a hot aqueous solution containing KF and K2[CO3] to another hot aquatic brine of Pr[NO3]3 ⋅ 5 H2O, Sm[NO3]3 ⋅ 5 H2O or Eu[NO3]3 ⋅ 5 H2O with a 1.3 times excess of the anion-providing solution, amorphous water-insoluble powders of PrF[CO3], SmF[CO3] and EuF[CO3] can be obtained. Through hydrothermal treatment at 210 °C for five days crystalline powders could be synthesized and their crystal structure was refined with Rietveld methods based on PXRD data. The named compounds crystallize in the bastnaesite-type structure with a = 710.912(12) pm, c = 976.811(6) pm for the praseodymium, a = 704.77(2) pm, c = 971.83(4) pm for the samarium and a = 700.734(6) pm, c = 969.066(8) pm for the europium compound, all hexagonal with Z = 6. Upon heating them, the compounds lose CO2 and fluoride oxides REFO emerge. Thermogravimetric experiments with crystalline samples show thermal stability up to 420 °C for PrF[CO3], 400 °C for SmF[CO3] and 340 °C for EuF[CO3], but decomposition below 200 °C for the amorphous ones. Infrared spectroscopy confirms only marginal portions of [OH]− instead of F− anions in all cases. The RE 3+ cations are coordinated by 9 + 2 anions at distances between 236 and 254 pm plus 326 pm to F− anions and oxygen atoms bonded to carbon as oxocarbonate anions [CO3]2−. Triggered by ultraviolet radiation, the bulk sample of EuF[CO3] shows a poor red luminescence.

From SmOF to SmH0.78OF0.22: H/F Substitution in Oxide Fluorides as a Synthesis Route to Heteroanionic Compounds

Mixed anionic hydrides of the rare earths are a fascinating class of compounds as potential functional materials, especially in luminescence, as photochromic thin films and for ion conduction. For exploratory studies, the effectiveness of various synthesis methods must be investigated, which is done here for metathesis reactions. The reaction of Sm₂O₃ with PTFE yields SmOF (P2₁/c, a = 5.60133(19) Å, b = 5.65567(19) Å, c = 5.6282(2) Å, β = 90.169(5)°, V = 178.295(11) ų, and Z = 4) in a new, probably metastable, polymorph of the baddeleyite-type structure. Metathesis reactions of SmOF with LiH, NaH, or CaH₂ led to a samarium hydride oxide fluoride, SmH_xOF_1-x; i.e., incomplete H/F exchange occurs. X-ray diffraction and neutron diffraction on a compound with x = 0.78 obtained via NaH reveal hydride, oxide, and fluoride ions to be partially ordered. SmH_0.78OF_0.22 (Ia3̅, a = 10.947(2) Å, V = 1311.7(4) ų, Z = 32) crystallizes in an anti-Li₃AlN₂-type structure with distorted cubic anion coordination for samarium atoms (site symmetry 3̅ and 2) and distorted tetrahedral arrangement of samarium atoms around the anions (site symmetry 1 and 3). It is a fully structurally characterized hydride oxide fluoride and shows a rare crystal chemical feature─the occupation of a crystallographic site by three different anions (0.188 H + 0.667 O + 0.145 F). Interatomic distances between samarium and hydrogen and samarium and the mixed hydrogen/oxygen/fluorine site range from 2.45 to 2.48 Å and 2.29 to 2.42 Å, respectively, and are similar to those in samarium hydride, samarium oxide, and samarium fluoride. Fluoride extraction by reaction with alkali and alkaline earth hydrides has thus proven to be a useful synthesis route to hydride oxides and also hydride oxide halogenides, which might be further exploited in exploratory research on heteroanionic metal hydrides.