Rheological comparison of organogelators based on iron and aluminum complexes of dodecylmethylphosphinic acid and methyl dodecanephosphonic acid

Thermally induced structural transformations of linear coordination polymers based on aluminum tris(diorganophosphates)

The thermal transitions of inorganic-organic hybrid polymers composed of linear aluminum tris(diorganophosphate) chains with a general formula of catena-Al[O2P(OR)2]3 (where R = C1-C8 alkyl group or phenyl moiety) have been studied by means of DSC, powder XRD, TGA and TG-QMS, as well as optical spectroscopy. DSC and XRD reveal that most of them undergo reversible structural transformations in the solid state between -100 and 200 °C caused by the changes in conformation of their organic substituents; however, a translational displacement of the rigid polymeric chains occurs only in the case of the derivative bearing long 2-ethylhexyl groups, which becomes liquid at about 140 °C. The thermal decomposition of the studied polymers begins between 200 and 265 °C depending on the type of organic substituent R decorating their aluminophospate core. TGA combined with mass spectrometry of the evolved gaseous products shows that the pyrolytic decomposition of Al[O2P(OR)2]3 proceeds either through β-elimination of olefin (for compounds with C2-C8 aliphatic ligands), or a homolytic cleavage of the P-OR bond (for methyl and phenyl derivatives); both processes are accompanied by condensation of the newly formed POH groups and liberation of water. Powder XRD, FTIR and SEM analyses of the solid residues indicate that thermolysis of Al[O2P(OR)2]3 accompanied by olefin elimination leads to the formation of condensed aluminum phosphates, mainly aluminum cyclohexaphosphate, exhibiting porous morphology. On the other hand, thermal degradation of methyl or phenyl derivatives results in amorphous aluminophosphate residues, and the latter contains conducting carbonaceous phases.

Linear coordination polymers based on aluminum phosphates: synthesis, crystal structure and morphology

Several aluminum tris(diorganophosphates) have been synthesized and characterized via elemental analysis, NMR, FT-IR and Raman spectroscopy, as well as powder XRD, and SEM. Single-crystal X-ray diffraction studies revealed that the aluminum tris(diethylphosphate) crystal structure comprises two crystallographically nonequivalent catena-Al[O2P(OEt)2]3 chains propagating along the c-axis. Their parallel orientation favors the formation of closely packed hexagonal domains. PXRD data suggest that other homologues have a similar structure, with the interchain distance closely corresponding to the dimensions of organic ligands. They are also susceptible to a reversible dissociation to ionic species under the effect of primary amines. This feature can be utilized for the synthesis of epoxy nanocomposites.