Stability of the parallel layer during alkane spreading and the domain structures of the standing-up layer

Spontaneous formation of nanopatterns in velocity-dependent dip-coated organic films: from dragonflies to stripes

We present an experimental study of the micro- and mesoscopic structure of thin films of medium length n-alkane molecules on the native oxide layer of a silicon surface, prepared by dip-coating in a n-C32H66/n-heptane solution. Electron micrographs reveal two distinct adsorption morphologies depending on the substrate withdrawal speed v. For small v, dragonfly-shaped molecular islands are observed. For a large v, stripes parallel to the withdrawal direction are observed. These have lengths of a few hundred micrometers and a few micrometer lateral separation. For a constant v, the stripes' quality and separation increase with the solution concentration. Grazing incidence X-ray diffraction and atomic force microscopy show that both patterns are 4.2 nm thick monolayers of fully extended, surface-normal-aligned alkane molecules. With increasing v, the surface coverage first decreases then increases for v > v(cr) ∼ 0.15 mm/s. The critical v(cr) marks a transition between the evaporation regime, where the solvent's meniscus remains at the bulk's surface, and the entrainment (Landau-Levich-Deryaguin) regime, where the solution is partially dragged by the substrate, covering the withdrawn substrate by a homogeneous film. The dragonflies are single crystals with habits determined by dendritic growth in prominent 2D crystalline directions of randomly seeded nuclei assumed to be quasi-hexagonal. The stripes' strong crystalline texture and the well-defined separation are due to an anisotropic 2D crystallization in narrow liquid fingers, which result from a Marangoni flow driven hydrodynamic instability in the evaporating dip-coated films, akin to the tears of wine phenomenology.

Octadecyltrichlorosilane (OTS)-coated ionic liquid drops: Micro-reactors for homogenous catalytic reactions at designated interfaces

An ionic liquid (IL), 1-butyl-3-methylimidazolium chloride ([Bmim]Cl) can assemble on prefabricated carboxylic acid-terminated chemical patterns on octadecyltrichlorosilane (OTS) film. The chemical pattern controls the position, shape and size of the IL on the surface. After the IL assembly - by incubating IL drops assembled on sample surface in an OTS silane vapor - an OTS layer was coated on the IL drop surface which encapsulated the IL drop. The OTS-coated capsule can exist stably under aqueous solution. The OTS coating protected the IL drops from being instantaneously dissolved by other solutions. We found that a homogenous catalyst (FeCl(3)) dissolved in [Bmim]Cl can be assembled together on the chemical patterns and subsequently encapsulated together with [Bmim]Cl by OTS coating. The pinhole defects within the vapor-coated silane layer provide space for the catalyst inside the capsule and reactants outside the capsule to meet and react. When the OTS-coated capsule containing a FeCl(3)/IL mixture was soaked under H(2)O(2) solution, the Fe(3+) ions catalyzed the decomposition reaction of hydrogen peroxide at the vapor-coated OTS-water interface. Since the shape and position of the interface is defined by the underneath chemical pattern, our findings show that the OTS-coated IL drops assembled on chemical patterns can be used as novel micro-reactors. This allows homogenous catalytic reactions to occur at the designated interfaces.

Molecular tilting and its impact on frictional properties of n-alkane self-assembled monolayers

Hydrophobic, methyl-terminated self-assembled monolayer (SAM) surfaces can be used to reduce friction. Among methyl-terminated SAMs, the frictional properties of alkanethiol SAMs and silane SAMs have been well-studied. In this research, we investigated friction of methyl-terminated n-hexatriacontane (C36) SAM and compared its friction properties with the alkanethiol and silane SAMs. Alkane SAM does not have an anchoring group. The alkane molecules stand on the surface by physical adsorption, which leads to a higher surface mobility of alkane molecules. We found that C36 SAM has a higher coefficient of friction than that of octadecyltrichlorosilane (OTS) silane. When an atomic force microscope (AFM) tip was swiped across the alkane SAM with a loading force, we found that the alkane SAM can withstand the tip loading pressure up to 0.48 GPa. Between 0.48 and 0.49Ga, the AFM tip partially penetrated the SAM. When the tip moved away, the deformed SAM healed and maintained the structural integrity. When the loading pressure was higher than 0.49 GPa, the alkane SAM was shaved into small pieces by the tip. In addition, we found that the molecular tilting of C36 molecules interacted with the tribological properties of the alkane SAM surface. On one hand, a higher loading force can push the rod-like alkane molecules to a higher tilting angle; on the other hand, a higher molecular tilting leads to a lower friction surface.