Synthesis, Structural Characterization, and Thermal and Optical Properties of Hyperbranched Poly(aminoarylene)s

Synthesis and properties of a novel highly thermal stable N-propargyl monomer containing benzoxazole ring

A novel highly thermal stable propargyl functional compound containing benzoxazole ring, N, N, N′, N′-tetra propargyl-5-amino-2-(p-aminophenyl) benzoxazole (TPAPB), was proposed and synthesized using a phase-transfer catalytic method. The cure behavior of TPAPB was investigated by non-isothermal differential scanning calorimetry analysis. The solubility and rheological properties of TPAPB, as well as its broad temperature window from 130°C to 200°C with low viscosity, offered excellent processability for TPAPB to be used as a potential monomer of thermosetting polymer resin. It was found that the glass transition temperature of cured TPAPB was 359°C, and the temperature of 5% weight loss was 418°C in argon with the char residue up to 70% at 700°C. The polymerized resin exhibited high heat resistance and thermal stability, together with its processability, making it good candidate as highly heat-resistant polymer matrix for advanced composite applications.

Development of a transition metal-free polymerization route to functional conjugated polydiynes from a haloalkyne-based organic reaction

Construction of functional polydiynes by transition metal-free homo-polycoupling of bis(iodoalkyne)s.

Functional hyperbranched polymers with advanced optical, electrical and magnetic properties

This review summarizes the recent progress in functional HBPs and their application in optics, electronics and magnetics, including light-emitting devices, aggregation-induced emission materials, nonlinear optical materials, chemosensors, solar cells, magnetic materials, etc., and provides outlooks for further exploration in the field.

Indium-catalyzed polycyclotrimerization of diynes: a facile route to prepare regioregular hyperbranched polyarylenes

The facile and efficient InCl₃/2-iodophenol-catalyzed polycyclotrimerization of diynes to generate regioregular hyperbranched polyarylenes was successfully established.

Synthesis and curing of hyperbranched poly(triazole)s with click polymerization for improved adhesion strength

We successfully synthesized hyperbranched poly(triazole)s by in situ click polymerization of diazides 1 and triyne 2 monomers on different metal surfaces (copper, iron, and aluminum) and characterized their adhesive properties. Optimizations were performed to obtain high adhesive strength at different temperatures by analyzing the effects of curing kinetics, annealing temperature and time, catalyst, monomer ratio, surface conditions, alkyl chain length of diazides 1, etc. The adhesive bonding strength with metal substrate is 2 orders of magnitude higher than similar hyperbranched poly(triazole)s made by click polymerization and clearly higher than some commercial adhesives at elevated temperatures. With the same conditions, adhesives prepared on aluminum and iron substrates have higher adhesive strength than those prepared on copper substrate, and an excess of triyne 2 monomer in synthesis has greater adhesive strength than an excess of diazide 1 monomer. Tof-SIMS experiment was employed to understand these phenomena, and the existence of an interphase between the polymer and metal surface was found to be critical for adhesive bonding with thicker interphase (excess of triyne 2 monomer) and the higher binding energy between polymer atoms and substrate atoms (e.g., aluminum substrate) generating the higher bonding strength. In addition, the light-emitting property of synthesized polymers under UV irradiation can be used to check the failure mode of adhesive bonding.