Unusual Surface Mechanical Properties of Poly(α-methylstyrene): Surface Softening and Stiffening at Different Temperatures

Polymers under nanoconfinement: where are we now in understanding local property changes?

Polymers are increasingly being used in applications with nanostructured morphologies where almost all polymer molecules are within a few tens to hundreds of nanometers from some interface. From nearly three decades of study on polymers in simplified nanoconfined systems such as thin films, we have come to understand property changes in these systems as arising from interfacial effects where local dynamical perturbations are propagated deeper into the material. This review provides a summary of local glass transition temperature T_g changes near interfaces, comparing across different types of interfaces: free surface, substrate, liquid, and polymer-polymer. Local versus film-average properties in thin films are discussed, making connections to other related property changes, while highlighting several historically important studies. By experimental necessity, most studies are on high enough molecule weight chains to be well entangled, although aspects that connect to lower molecule weight materials are described. Emphasis is made to identify observations and open questions that have yet to be fully understood such as the evidence of long-ranged interfacial effects, finite domain size, interfacial breadth, and chain connectivity.

Changes in the temperature-dependent specific volume of supported polystyrene films with film thickness

Recent studies have measured or predicted thickness-dependent shifts in density or specific volume of polymer films as a possible means of understanding changes in the glass transition temperature Tg(h) with decreasing film thickness with some experimental works claiming unrealistically large (25%-30%) increases in film density with decreasing thickness. Here we use ellipsometry to measure the temperature-dependent index of refraction of polystyrene (PS) films supported on silicon and investigate the validity of the commonly used Lorentz-Lorenz equation for inferring changes in density or specific volume from very thin films. We find that the density (specific volume) of these supported PS films does not vary by more than ±0.4% of the bulk value for film thicknesses above 30 nm, and that the small variations we do observe are uncorrelated with any free volume explanation for the Tg(h) decrease exhibited by these films. We conclude that the derivation of the Lorentz-Lorenz equation becomes invalid for very thin films as the film thickness approaches ∼20 nm, and that reports of large density changes greater than ±1% of bulk for films thinner than this likely suffer from breakdown in the validity of this equation or in the difficulties associated with accurately measuring the index of refraction of such thin films. For larger film thicknesses, we do observed small variations in the effective specific volume of the films of 0.4 ± 0.2%, outside of our experimental error. These shifts occur simultaneously in both the liquid and glassy regimes uniformly together starting at film thicknesses less than ∼120 nm but appear to be uncorrelated with Tg(h) decreases; possible causes for these variations are discussed.

Relationship between Segmental Relaxation of Polystyrene Films and Stick-Slip Behavior during Dynamic Wetting of Liquid Droplets on Their Surfaces

A novel method was previously reported for detecting the glass transition of thin polystyrene (PS) films by correlating the relationships between the temperature-dependent viscoelasticity of the PS films and stick-slip behavior on their surfaces during dynamic wetting of liquid droplets. In the present study, the frequency dependence of the stick-slip behavior is investigated. The results show that the stick-slip behavior of liquid dynamic wetting on PS films is dependent on the contact line velocity, which is related to the deformation frequency of the PS surface during the moving liquid front. The stick-slip behavior was revealed to be determined by a dimensionless parameter (ξ), which is the ratio of the PS segmental relaxation time (τα) and the characteristic time (τc) for PS surface deformation near the droplet contact line. When ξ is close to 1 (τα ≈ τc), the Δθ (jumping angle), a scale of the stick-slip behavior, reaches a maximum. This correlation between Δθ and ξ demonstrates that the stick-slip behavior is related to the energy dissipation caused by the PS α-relaxation process, and the peak temperature (or frequency) in Δθ corresponds to the α-relaxation temperature (time) of the polymer. These results strongly demonstrate that the utilization of the stick-slip behavior is a creditable method, similar to dynamic viscoelastic measurement, for probing the glass transition and segmental relaxation of thin polymer films.