Smart meta-superconductor MgB2 constructed by the dopant phase of luminescent nanocomposite

The Influence of Electroluminescent Inhomogeneous Phase Addition on Enhancing MgB2 Superconducting Performance and Magnetic Flux Pinning

As a highly regarded superconducting material with a concise layered structure, MgB2 has attracted significant scientific attention and holds vast potential for applications. However, its limited current-carrying capacity under high magnetic fields has greatly hindered its practical use. To address this issue, we have enhanced the superconducting performance of MgB2 by incorporating inhomogeneous phase nanostructures of p-n junctions with electroluminescent properties. Through temperature-dependent measurements of magnetization, electronic specific heat, and Hall coefficient under various magnetic fields, we have confirmed the crucial role of inhomogeneous phase electroluminescent nanostructures in improving the properties of MgB2. Experimental results demonstrate that the introduction of electroluminescent inhomogeneous phases effectively enhances the superconducting performance of MgB2. Moreover, by controlling the size of the electroluminescent inhomogeneous phases and optimizing grain connectivity, density, and microstructural uniformity, we can further improve the critical temperature (TC) and flux-pinning capability of MgB2 superconducting materials. Comprehensive studies on the physical properties of MgB2 superconducting structures added with p-n junction electroluminescent inhomogeneous phases also confirm the general effectiveness of electroluminescent inhomogeneous phases in enhancing the performance of superconducting materials.

An Improved Smart Meta-Superconductor MgB2

Increasing and improving the critical transition temperature (TC), current density (JC) and the Meissner effect (HC) of conventional superconductors are the most important problems in superconductivity research, but progress has been slow for many years. In this study, by introducing the p-n junction nanostructured electroluminescent inhomogeneous phase with a red wavelength to realize energy injection, we found the improved property of smart meta-superconductors MgB2, the critical transition temperature TC increases by 0.8 K, the current density JC increases by 37%, and the diamagnetism of the Meissner effect HC also significantly improved, compared with pure MgB2. Compared with the previous yttrium oxide inhomogeneous phase, the p-n junction has a higher luminescence intensity, a longer stable life and simpler external field requirements. The coupling between superconducting electrons and surface plasmon polaritons may be explained by this phenomenon. The realization of smart meta-superconductor by the electroluminescent inhomogeneous phase provides a new way to improve the performance of superconductors.

Critical Current Density and Meissner Effect of Smart Meta-Superconductor MgB2 and Bi(Pb)SrCaCuO

The smart meta-superconductor MgB2 and Bi(Pb)SrCaCuO increase the superconducting transition temperature (TC), but the changes in the transport critical current density (JC) and Meissner effect are still unknown. Here, we investigated the JC and Meissner effect of smart meta-superconductor MgB2 and Bi(Pb)SrCaCuO. The use of the standard four-probe method shows that Y2O3:Eu3+ and Y2O3:Eu3++Ag inhomogeneous phase significantly increase the JC, and JC decreases to a minimum value at a higher temperature. The Meissner effect was measured by direct current magnetization. The doping of Y2O3:Eu3+ and Y2O3:Eu3++Ag luminescent inhomogeneous phase causes a Meissner effect of MgB2 and Bi(Pb)SrCaCuO at a higher temperature, while the non-luminescent dopant reduces the temperature at which samples have Meissner effect. The introduction of luminescent inhomogeneous phase in conventional MgB2 and copper oxide high-temperature Bi(Pb)SrCaCuO superconductor increases the TC and JC, and Meissner effect is exerted at higher temperature. Therefore, smart meta-superconductivity is suitable for conventional and copper oxide high-temperature superconductors.

Reinforcing Increase of ΔTc in MgB2 Smart Meta-Superconductors by Adjusting the Concentration of Inhomogeneous Phases

Incorporating with inhomogeneous phases with high electroluminescence (EL) intensity to prepare smart meta-superconductors (SMSCs) is an effective method for increasing the superconducting transition temperature (T_c) and has been confirmed in both MgB₂ and Bi(Pb)SrCaCuO systems. However, the increase of ΔT_c (ΔT_c = T_c ‒ T_cpure) has been quite small because of the low optimal concentrations of inhomogeneous phases. In this work, three kinds of MgB₂ raw materials, namely, ^aMgB₂, ^bMgB₂, and ^cMgB₂, were prepared with particle sizes decreasing in order. Inhomogeneous phases, Y₂O₃:Eu³⁺ and Y₂O₃:Eu³⁺/Ag, were also prepared and doped into MgB₂ to study the influence of doping concentration on the ΔT_c of MgB₂ with different particle sizes. Results show that reducing the MgB₂ particle size increases the optimal doping concentration of inhomogeneous phases, thereby increasing ΔT_c. The optimal doping concentrations for ^aMgB₂, ^bMgB₂, and ^cMgB₂ are 0.5%, 0.8%, and 1.2%, respectively. The corresponding ΔT_c values are 0.4, 0.9, and 1.2 K, respectively. This work open a new approach to reinforcing increase of ΔT_c in MgB₂ SMSCs.

Relationship between the TC of Smart Meta-Superconductor Bi(Pb)SrCaCuO and Inhomogeneous Phase Content

A smart meta-superconductor Bi(Pb)SrCaCuO (B(P)SCCO) may increase the critical transition temperature (T_C) of B(P)SCCO by electroluminescence (EL) energy injection of inhomogeneous phases. However, the increase amplitude ΔT_C (ΔTC=TC−TC,pure) of T_C is relatively small. In this study, a smart meta-superconductor B(P)SCCO with different matrix sizes was designed. Three kinds of raw materials with different particle sizes were used, and different series of Y₂O₃:Sm³⁺, Y₂O₃, Y₂O₃:Eu³⁺, and Y₂O₃:Eu³⁺+Ag-doped samples and pure B(P)SCCO were prepared. Results indicated that the T_C of the Y₂O₃ or Y₂O₃:Sm³⁺ non-luminescent dopant doping sample is lower than that of pure B(P)SCCO. However, the T_C of the Y₂O₃:Eu³⁺+Ag or Y₂O₃:Eu³⁺ luminescent inhomogeneous phase doping sample is higher than that of pure B(P)SCCO. With the decrease of the raw material particle size from 30 to 5 μm, the particle size of the B(P)SCCO superconducting matrix in the prepared samples decreases, and the doping content of the Y₂O₃:Eu³⁺+Ag or Y₂O₃:Eu³⁺ increases from 0.2% to 0.4%. Meanwhile, the increase of the inhomogeneous phase content enhances the ΔT_C. When the particle size of raw material is 5 μm, the doping concentration of the luminescent inhomogeneous phase can be increased to 0.4%. At this time, the zero-resistance temperature and onset transition temperature of the Y₂O₃:Eu³⁺+Ag doped sample are 4 and 6.3 K higher than those of pure B(P)SCCO, respectively.