A highly elastic absorbable monofilament suture fabricated from poly(3-hydroxybutyrate-co-4-hydroxybutyrate)

Production and Characterization of Melt-Spun Poly(3-hydroxybutyrate)/Poly(3-hydroxybutyrate-co-4-hydroxybutyrate) Blend Monofilaments

We investigated the melt-spinning potential of a poly(3-hydroxybutyrate)/poly(3-hydroxybutyrate-co-4-hydroxybutyrate) blend using a piston spinning machine with two different spinneret diameters (0.2 and 0.5 mm). Results from the differential scanning calorimetry, dynamic mechanical thermal analysis, and tensile testing showed distinct filament properties depending on the monofilaments' cross-sectional area. Finer filaments possessed different melting behaviors compared to the coarser filaments and the neat polymer, indicating the formation of a different type of polymer crystal. Additionally, the mechanical properties of the finer filament (tensile strength: 21.5 MPa and elongation at break: 341%) differed markedly from the coarser filament (tensile strength: 11.7 MPa, elongation at break: 12.3%). The hydrolytic stability of the filaments was evaluated for 7 weeks in a phosphate-buffered saline solution and showed a considerably reduced elongation at break of the thinner filaments. Overall, the results indicate considerable potential for further filament improvements to facilitate textile processing.

Marine biodegradation of poly[(R)-3-hydroxybutyrate-co-4-hydroxybutyrate] elastic fibers in seawater: dependence of decomposition rate on highly ordered structure

Here, we report the marine degradability of polymers with highly ordered structures in natural environmental water using microbial degradation and biochemical oxygen demand (BOD) tests. Three types of elastic fibers (non-porous as-spun, non-porous drawn, and porous drawn) with different highly ordered structures were prepared using poly[(R)-3-hydroxybutyrate-co-16 mol%-4-hydroxybutyrate] [P(3HB-co-16 mol%-4HB)], a well-known polyhydroxyalkanoate. Scanning electron microscopy (SEM) images indicated that microorganisms attached to the fiber surface within several days of testing and degraded the fiber without causing physical disintegration. The results of BOD tests revealed that more than 80% of P(3HB-co-16 mol%-4HB) was degraded by microorganisms in the ocean. The plastisphere was composed of a wide variety of microorganisms, and the microorganisms accumulated on the fiber surfaces differed from those in the biofilms. The microbial degradation rate increased as the degree of molecular orientation and porosity of the fiber increased: as-spun fiber < non-porous drawn fiber < porous drawn fiber. The drawing process induced significant changes in the highly ordered structure of the fiber, such as molecular orientation and porosity, without affecting the crystallinity. The results of SEM observations and X-ray measurements indicated that drawing the fibers oriented the amorphous chains, which promoted enzymatic degradation by microorganisms.