Coupled crystal orientation-size effects on the strength of nano crystals

Polymer-Controlled Growth and Wrapping of Perovskite Single Crystals Leading to Better Device Stability and Performance

A commodity-scale polymer is used for controlling the nucleation and growth of single crystals of organolead halide perovskite. The polymer [polystyrene (PS)] cross-links and strongly interacts with PbI₂ and MAI (MAPbI₃ perovskite precursors) resulting in the control of the crystallization process. The PS concentration modulates the nucleation time, crystal size, and the number of perovskite single crystals. In addition, the PS-based MAPbI₃ crystals show an enhanced performance as well as improved thermal and environmental stability. Specifically, the PS-MAPbI₃ crystals show 3 times higher photocurrent than plain MAPbI₃ crystals and maintain a stable structure for more than 50 days (1200 h) under continuous 0.1 sun illumination in the air with a relative humidity of 40-45%. The improved performance and stability are attributed to the direct interaction between the PS and perovskite, which greatly reduces the ion migration, defect traps, and charge recombination and improves the carrier mobility and lifetime.

Comparative Study on Microstructural Stability of Pre-annealed Electrodeposited Nanocrystalline Nickel During Pack Rolling

Microstructural stability is an important issue for nanocrystalline materials to be practically used in many fields. The present work shows how microstructure evolves with rolling strain in pre-annealed electrodeposited nanocrystalline nickel containing an initial strong fiber texture, on the basis of X-ray diffraction line profile analysis as well as transmission electron microscopy observation. The influence of shear strain on microstructural stability of the metal/roll contact interface is compared with that of the metal/metal contact interface; the latter would be closer to deformation in plane strain compression. From the statistical microstructural information, together with experimentally observed microstructure of deformed grains after the final rolling pass, it seems fair to conclude that the microstructure of the metal/metal contact interface is more stable during pack rolling than that of the metal/roll interface.