Synthesis and structure analysis of (K[DB18 C6])4(C60)5·12THF containing C60 in three different bonding states

A new fulleride, (K[DB18C6])(4)(C(60))(5)·12THF, was prepared in solution using the "break-and-seal" approach by reacting potassium, fullerene, and dibenzo[18]crown-6 in tetrahydrofuran. Single crystals were grown from solution by the modified "temperature difference method". X-ray analysis was performed revealing a reversible phase transition occurring on cooling. Three different crystal structures of the title compound at different temperatures of data acquisition are addressed in detail: the "high-temperature phase" at 225 K (C2, Z=2, a=49.055(1), b=15.075(3), c=18.312(4) Å, β=97.89(3)°), the "transitional phase" at 175 K (C2 m, Z=2, a=48.436(5), b=15.128(1), c=18.280(2) Å, β=97.90(1)°), and the "low-temperature phase" at 125 K (Cc, Z=4, a=56.239(1), b=15.112(3), c=36.425(7) Å, β=121.99(1)°). On cooling, partial radical recombination of C(60)(·-) into the (C(60))(2)(2-) dimeric dianion occurs; this is first time that the fully ordered dimer has been observed. Further cooling leads to formation of a superstructure with doubled cell volume in a different space group. Below 125 K, C(60) exists in the structure in three different bonding states: in the form of C(60)(·-) radical ions, (C(60))(2)(2-) dianions, and neutral C(60), this being without precedent in the fullerene chemistry, as well. Experimental observations of one conformation exclusively of the fullerene dimer in the crystal structure are further explained on the basis of DFT calculations considering charge distribution patterns. Temperature-dependent measurements of magnetic susceptibility at different magnetic fields confirm the phase transition occurring at about 220 K as observed crystallographically, and enable for unambiguous charge assignment to the different C(60) species in the title fulleride.

Neutral and Ionic Complexes of C60 with Metal Dibenzyldithiocarbamates. Reversible Dimerization of C60•- in Ionic Multicomponent Complex [CrI(C6H6)2•+]·(C60•-)·0.5[Pd(dbdtc)2]

New molecular complexes of C60 with metal(II) dibenzyldithiocarbamates, M(dbdtc)2.C60.0.5(C6H5Cl), where M=Cu(II), Ni(II), Pd(II), and Pt(II) and an ionic multicomponent complex [Cr(I)(C6H6)2*+].(C60*-).0.5[Pd(dbdtc)2] (Cr(C6H6)2: bis(benzene)chromium) were obtained. According to IR, UV-visible-NIR, and EPR spectra, involve neutral components, whereas 5 comprises neutral Pd(dbdtc)2 and C60*- and Cr(I)(C6H6)2*+ radical ions. The crystal structure of at 90 K reveals strongly puckered fullerene layers alternating with those composed of Pd(dbdtc)2. The Cr(I)(C6H6)2*+ radical cations are arranged between the layers. Fullerene radical anions form pairs within the layer with an interfullerene C...C contact of 3.092(2) A, indicating their monomeric state at 90 K. This contact is essentially shorter than the sum of van der Waals radii of two carbon atoms, and consequently, C60*- can dimerize. According to SQUID and EPR, single-bonded diamagnetic (C60-)2 dimers form in below 150-130 K on slow cooling and dissociate above 150-170 K on heating. The hysteresis was estimated to be 20 K. For the (C60-)2 dimers in, the dissociation temperature is the lowest among those for ionic complexes of C60 (160-250 K). Fast cooling of the crystals within 10 min from room temperature down to 100 K shifts dimerization temperatures to lower than 60 K. This shift is responsible for the retention of a monomeric phase of at 90 K in the X-ray diffraction experiment.