Electrodeposition of tin nanowires from a dichloromethane based electrolyte

Tin was electrodeposited from a dichloromethane-based electrolyte at ambient temperature into gold coated anodic alumina membranes with nanoscale pores. The tin nanowires are mainly 〈200〉 aligned, together with some 〈101〉 and 〈301〉 wires. Partial filling of the structure and a distribution of wire lengths was found. Grafting of the pores with hydrophobic surface groups was trialled as a means of modifying the deposition, however, it did not increase the proportion of pores in which wires grew. Under potentiostatic conditions the limited rates of nucleation and diffusion down the 1D pores control the growth of the nanowires.

Chemoselective nanoporous membranes via chemically directed assembly of nanoparticles and dendrimers

Chemoselective nanoporous membranes: tunably porous membranes with embedded functionalities are generated using a template-free, chemically directed nanoparticle-dendrimer (NP-Den) network assembly. This approach provides a direction in the design of post-functionalizable nanoporous membranes for distinguishing both organic molecules and proteins with excellent chemo- and bioselectivity.

Mesostructured silica containing conjugated polymers formed within the channels of anodic alumina membranes from tetrahydrofuran-based solution

The synthesis of mesostructured silica from a tetrahydrofuran (THF)-based sol gel was carried out in the channels of an anodic alumina membrane (AAM) using the evaporation-induced self-assembly (EISA) method. Two different nonionic surfactants were used as structure-directing agents, the triblock copolymer Pluronic P123 and the oligomer surfactant Brij56. The effect of the relative humidity and surfactant concentration on the type of mesophase and orientation of the in-channel mesostructures was studied using transmission electron microscopy (TEM) and grazing incidence small angel X-ray scattering (GISAXS). The in-channel structures obtained in this study were primarily of the 2D hexagonal phase with a circular orientation in which the hexagonally packed cylinders form a spiral-like shape from the channel wall inward. In addition, a columnar orientation of the hexagonal phase, in which the axes of the hexagonally packed cylinders are oriented parallel to the channel axes, was also observed. Finally, the use of the THF-based synthesis allowed the in situ incorporation of the highly hydrophobic yellow-emitting conjugated polymer poly[9,9-dioctylfluorene-co-benzothiadiazole] into the in-channel mesostructure upon its formation. The conjugated polymer was well distributed within the mesostructure and maintained its optical properties.

Mesoporous structures confined in anodic alumina membranes

The synthesis of nanoporous membranes based on different concepts and materials is a field of active research. This review focuses on the synthesis strategies, mesophase evolution mechanisms and potential applications of mesoporous materials confined within anodic alumina membranes (AAM). Following a rapid evolution of synthetic techniques, a significant number of different mesoporous materials (e.g., silica, titania, and carbon) with highly regular structures can now be prepared within these membranes. In recent years, efforts have also been made to understand the formation mechanisms of these hierarchical mesophases. The resulting organized nanoporous membranes open up a wide range of potential applications in fields such as templating oriented nanowires and controlled separation and release of molecules. For example, while various synthesis strategies can be used for the preparation of membrane-embedded nanowires, the latter can also be obtained as isolated objects after dissolution of the alumina host matrix. The review also discusses issues such as control of structural defects or integrity of interfaces that should be addressed in future research in order to fully exploit the potential of these hierarchical mesoporous channel structures.