Preparation and Photocatalytic Properties of Anatase TiO2 with Hollow Hexagonal Frame Structure

Titanium dioxide (TiO2) has been widely used to solve energy and environmental pollution problems due to its excellent properties. In this study, the precursor (HTiOF3) with a spherical structure composed of hexagonal prisms was prepared via a simple solvothermal method using tetrabutyl titanate, hydrofluoric acid, glacial acetic acid and isopropanol as raw materials. Then, the calcination time and temperature of the precursor were controlled to prepare anatase TiO2 with different morphologies, and the photocatalytic performance of the prepared catalysts was studied. When the precursor was calcined at 600 °C for 7 h, the prepared TiO2 had a unique hexagonal framework structure and exhibited excellent photocatalytic performance. The degradation rate of the RhB solution was 98.58% at 40 min and the rate of hydrogen evolution was 2508.12 μmol g−1 h−1.

Facile Formation of Anatase Nanoparticles on H-Titanate Nanotubes at Low Temperature for Efficient Visible Light-Driven Degradation of Organic Pollutants

Anatase nanoparticles (5–10 nm) generated on H-titanate nanotube surface (H-titanate/anatase) were prepared by an ingenious and simple method. H-titanate tubes were prepared by a hydrothermal reaction of Ti powder in concentrated NaOH solution and an ion exchange process with HNO3 solution. After that, at a relatively low drying temperature (100 °C), a small quantity of anatase nanoparticles were in-situ formed on the H-titanate tubes surface by a surface dehydration reaction. In-situ transformation can form a strong interface coupling between H-titanate and anatase, which is conducive to accelerating charge transfer and improving its photocatalytic activity. In addition, the smaller average crystal size, the large specific surface areas (BET), the nanotubed and layered structure and the synergistic effect of dual phases would be beneficial to improving the photocatalytic efficiency.

Fabrication of a high-adsorption N–TiO2/Bi2MoO6 composite photocatalyst with a hierarchical heterostructure for boosted weak-visible-light photocatalytic degradation of tetracycline

TiO₂ hierarchical heterostructure photocatalyst was successfully fabricated through the in situ growth of Bi₂MoO₆ nanosheets on rough N–TiO₂ nanorods with a bark-like surface. The structure–property relationship of this composite material were researched.

Mesoporous TiO2 core-shell spheres composed of nanocrystals with exposed high-energy facets: facile synthesis and formation mechanism

A facile new method that combines electrospray and hydrothermal treatment is used to prepare mesoporous core-shell TiO(2) spheres with high specific surface areas and high pore volumes. Interestingly, the resulting TiO(2) spheres are composed of anatase TiO(2) nanocrystals with exposed step-like {001} and smooth {010} facets. The percentage of exposed {001} facets can be adjusted by changing the experimental parameters used in the electrospray and hydrothermal treatment processes, such as the contents of poly(N-vinyl-2-pyrrolidone) and acetic acid. The combination of high specific surface area (>100 m(2) g(-1)), high pore volume (>0.30 cm(3) g(-1)), useful pore size (10-15 nm), spherical core-shell structure, and exposed high energy facets makes these TiO(2) spheres an important candidate for use in many photoelectrochemical applications. The formation mechanism of the mesoporous TiO(2) spheres is also studied. The great advantage of this method is that interesting and complicated mesoporous superstructures can be prepared using electrospray technology.