Confined water radiolysis in aluminosilicate nanotubes: the importance of charge separation effects

Imogolite nanotubes are potentially promising co-photocatalysts because they are predicted to have curvature-induced, efficient electron-hole pair separation. This prediction has however not yet been experimentally proven. Here, we investigated the behavior upon irradiation of these inorganic nanotubes as a function of their water content to understand the fate of the generated electrons and holes. Two types of aluminosilicate nanotubes were studied: one was hydrophilic on its external and internal surfaces (IMO-OH) and the other had a hydrophobic internal cavity due to Si-CH₃ bonds (IMO-CH₃), with the external surface remaining hydrophilic. Picosecond pulse radiolysis experiments demonstrated that the electrons are efficiently driven outward. For imogolite samples with very few external water molecules (around 1% of the total mass), quasi-free electrons were formed. They were able to attach to a water molecule, generating a water radical anion, which ultimately led to dihydrogen. When more external water molecules were present, solvated electrons, precursors of dihydrogen, were formed. In contrast, holes moved towards the internal surface of the tubes. They mainly led to the formation of dihydrogen and of methane in irradiated IMO-CH₃. The attachment of the quasi-free electron to water was a very efficient process and accounted for the high dihydrogen production at low relative humidity values. When the water content increased, electron solvation dominated over attachment to water molecules. Electron solvation led to dihydrogen production, albeit to a lesser extent than quasi-free electrons. Our experiments demonstrated the spontaneous curvature-induced charge separation in these inorganic nanotubes, making them very interesting potential co-photocatalysts.

100th Anniversary of Macromolecular Science Viewpoint: Polymeric Materials by In Situ Liquid-Phase Transmission Electron Microscopy

A century ago, Hermann Staudinger proposed the macromolecular theory of polymers, and now, as we enter the second century of polymer science, we face a different set of opportunities and challenges for the development of functional soft matter. Indeed, many fundamental questions remain open, relating to physical structures and mechanisms of phase transformations at the molecular and nanoscale. In this Viewpoint, we describe efforts to develop a dynamic, in situ microscopy tool suited to the study of polymeric materials at the nanoscale that allows for direct observation of discrete structures and processes in solution, as a complement to light, neutron, and X-ray scattering methods. Liquid-phase transmission electron microscopy (LPTEM) is a nascent in situ imaging technique for characterizing and examining solvated nanomaterials in real time. Though still under development, LPTEM has been shown to be capable of several modes of imaging: (1) imaging static solvated materials analogous to cryo-TEM, (2) videography of nanomaterials in motion, (3) observing solutions or nanomaterials undergoing physical and chemical transformations, including synthesis, assembly, and phase transitions, and (4) observing electron beam-induced chemical-materials processes. Herein, we describe opportunities and limitations of LPTEM for polymer science. We review the basic experimental platform of LPTEM and describe the origin of electron beam effects that go hand in hand with the imaging process. These electron beam effects cause perturbation and damage to the sample and solvent that can manifest as artefacts in images and videos. We describe sample-specific experimental guidelines and outline approaches to mitigate, characterize, and quantify beam damaging effects. Altogether, we seek to provide an overview of this nascent field in the context of its potential to contribute to the advancement of polymer science.

Reaction mechanisms in swelling clays under ionizing radiation: influence of the water amount and of the nature of the clay mineral

Picosecond pulse radiolysis experiments performed on natural swelling clays evidence a fast trapping of electrons in the layers of the material.

Radiolytic synthesis of Au–Cu bimetallic nanoparticles supported on TiO2: application in photocatalysis

The modification of TiO₂ with Au–Cu nanoalloys (synthesized by radiolysis after deposition–precipitation in the presence of urea) induces an enhancement in the photocatalytic activity under UV light.

Water radiolysis in exchanged-montmorillonites: the H2 production mechanisms

The radiolysis of water confined in montmorillonites is studied as a function of the composition of the montmorillonite, the nature of the exchangeable cation, and the relative humidity by following the H2 production under electron irradiation. It is shown that the main factor influencing this H2 production is the water amount in the interlayer space. The effect of the exchangeable cation is linked to its hydration enthalpy. When the water amount is high enough to get a basal distance higher than 1.3 nm, then a total energy transfer from the montmorillonite sheets to the interlayer space occurs, and the H2 production measured is very similar to the one obtained in bulk water. For a basal distance smaller than 1.3 nm, the H2 production increases with the relative humidity and thus with the water amount. Lastly, electron paramagnetic resonance measurements evidence the formation of a new defect induced by ionizing radiation. It consists of a hydrogen radical (H2 precursor) trapped in the structure. This implies that structural hydroxyl bonds can be broken under irradiation, potentially accounting for the observed H2 production.