Carbon nanofibres from fructose using a light-driven high-temperature spinning disc processor

Recent advancements in lignocellulose biomass-based carbon fiber: Synthesis, properties, and applications

A growing need to reduce the global carbon footprint has prompted all sectors to make significant efforts in this direction. For example, there has been much focus on green carbon fiber sustainability. For example, it was found that the polyaromatic heteropolymer lignin might act as an intermediary in synthesising carbon fiber. Biomass is seen as a potential carbon accommodated solid natural sources that protects the nature and has a big overall supply and widespread distribution. With growing environmental concern in recent years, biomass has gained appeal as a raw material for production of carbon fibers. Especially, the positives of lignin material include its reasonable budget, sustainability, and higher carbon content, which makes it a dominating precursor. This review has examined a variety of bio precursors that help produce lignin and have higher lignin concentrations. In addition, there has been much research on plant sources, lignin types, factors affecting carbon fiber synthesis, spinning methods, stabilization, carbonization, and activation the characterisation techniques used for the lignin carbon fiber to comprehend the structure and features. In addition, an overview of the applications that use lignin carbon fiber has been provided.

Waste NR Latex Based-Precursors as Carbon Source for CNTs Eco-Fabrications

In this work, the potential of utilizing a waste latex-based precursor (i.e., natural rubber glove (NRG)) as a carbon source for carbon nanotube (CNT) fabrication via chemical vapor deposition has been demonstrated. Gas chromatography-mass spectroscopy (GC-MS) analysis reveals that the separation of the lightweight hydrocarbon chain from the heavier long chain differs in hydrocarbon contents in the NRG fraction (NRG-L). Both solid NRG (NRG-S) and NRG-L samples contain >63% carbon, <0.6% sulfur and <0.08% nitrogen content, respectively, as per carbon-nitrogen-sulfur (CNS) analysis. Growth of CNTs on the samples was confirmed by Raman spectra, SEM and TEM images, whereby it was shown that NRG-S is better than NRG-L in terms of synthesized CNTs yield percentage with similar quality. The optimum vaporization and reaction temperatures were 350 and 800 °C, respectively, considering the balance of good yield percentage (26.7%) and quality of CNTs (I_D/I_G = 0.84 ± 0.08, diameter ≈ 122 nm) produced. Thus, utilization of waste NRG as a candidate for carbon feedstock to produce value-added CNTs products could be a significant approach for eco-technology.

Synthesis of Carbon Nanotube Arrays with High Aspect Ratio via Ni-Catalyzed Pyrolysis of Waste Polyethylene

Carbon nanotube (CNT) arrays 30–50 nm in diameter and with a length of several micrometers were prepared by catalytic pyrolysis of waste polyethylene in Ar at 773−1073 K using nickel dichloride as a catalyst precursor. X-ray diffraction (XRD), scanning electron microscopy (SEM), Raman spectrometry (Raman), a vibrating-sample magnetometer (VSM), and nitrogen adsorption/desorption were used to investigate the effects of the pyrolysis temperature and catalyst contents on the preparation of the aligned CNTs. As results, the as-obtained CNTs had an outer diameter of 30 nm, a wall thickness of 10 nm, and a length of about 50 μm, and their aspect ratio was high up to 1500. The aligned CNTs containing 0.75 wt% Ni prepared at 973 K exhibited good adsorption performance for methylene blue (MB); furthermore, benefiting from the special magnetic properties of residual Ni catalysts, the as-obtained CNTs could be easily magnetically recycled from the treated solution after adsorption.

Formation of carbon nanosheets via simultaneous activation and catalytic carbonization of macroporous anion-exchange resin for supercapacitors application

Two-dimensional mesoporous carbon nanosheets (CNSs) have been prepared via simultaneous activation and catalytic carbonization route using macroporous anion-exchange resin (AER) as carbon precursor and ZnCl2 and FeCl3 as activating agent and catalyst, respectively. The iron catalyst in the skeleton of the AER may lead to carburization to form a sheetlike structure during the carbonization process. The obtained CNSs have a large number of mesopores, a maximum specific surface area of 1764.9 m(2) g(-1), and large pore volume of 1.38 cm(3) g(-1). As an electrode material for supercapacitors application, the CNSs electrode possesses a large specific capacitance of 283 F g(-1) at 0.5 A g(-1) and excellent rate capability (64% retention ratio even at 50 A g(-1)) in 6 mol L(-1) KOH. Furthermore, CNSs symmetric supercapacitor exhibits specific energies of 17.2 W h kg(-1) at a power density of 224 W kg(-1) operated in the voltage range of 0-1.8 V in 0.5 mol L(-1) Na2SO4 aqueous electrolyte, and outstanding cyclability (retains about 96% initial capacitance after 5000 cycles).