Production of Oximes Directly from Sustainable Lignocellulose-Derived Aldehydes and Ammonia over HTS-1 Catalyst

Oxime chemicals are the building blocks of many anticancer drugs and widely used in industry and laboratory. A simple but robust hierarchically porous zeolite (HTS-1) catalyst was prepared by hydrothermal methods and used for the preparation of vanillin oxime from vanillin in NH3  ⋅ H2 O/DIO (v/v 1/10) system. The results of the catalyst characterization showed that the larger pore size and more framework Ti were conducive to promote the transformation of the substrates. The conversion of vanillin and the yield of vanillin oxime were both higher than 99 % under optimized reaction conditions. It was found that the reaction proceeded by oxidation of NH3 to hydroxylamine (NH2 OH), and oximation of hydroxylamine with vanillin to obtain vanillin oxime, where the rate-controlling step was the hydroxylamine formation, and the apparent activation energy was 26.22 kJ/mol. The corresponding oximation products could also be obtained by extending this method to other compounds derived from lignin. Furthermore, the catalytic system was used directly to the conversion of birch biomass to obtain oxime products such as vanillin oxime, syringaldehyde oxime, and furfural oxime etc. This work might give insights into the sustainable production of N-containing high-value products from lignocellulose.

The Clean Synthesis of Small-Particle TS-1 with High-Content Framework Ti by Using NH4HCO3 and Suspended Seeds as an Assistant

The synthesis of a TS-1 zeolite with high-content framework Ti and small particles has been developed by adding NH₄HCO₃ and suspended seeds as an assistant. With the addition of NH₄HCO₃, the Hofmann decomposition of the tetrapropylammonium cation (TPA⁺) decreased, and the framework Ti content of the zeolite increased first and then decreased while the particle became larger. With the assistance of suspended seeds, the TS-1 synthesized under a low-alkalinity system possesses small particle size and high-content framework Ti, and it shows the best catalytic activity among the prepared catalysts. Because the decomposition of TPA⁺ decreased, the mother liquid could be reused in the next run of preparation. Even though the recycled mother liquid was reused five times, all obtained TS-1 samples exhibited similar catalytic performances in propylene epoxidation. This work provides an efficient process for preparing TS-1 with good catalytic performance and reduces the discharge of the waste liquid.

Al-Modified Ti-MOR as a robust catalyst for cyclohexanone ammoximation with enhanced anti-corrosion performance

The skeleton desilication accompanied by Ti active sites leaching accounts for the dominant chemical deactivation reasons in the alkali liquid-phase ammoximation, which could be retarded by creating a protective Al-rich shell.

Selective synthesis of epichlorohydrin via liquid-phase allyl chloride epoxidation over a modified Ti-MWW zeolite in a continuous slurry bed reactor

The epoxidation of allyl chloride (ALC) to epichlorohydrin (ECH) with H₂O₂ using a piperidine (PI)-modified Ti-MWW catalyst (Ti-MWW-PI) in a continuous slurry reactor was investigated to develop an efficient reaction system for the corresponding industrial process.

Improved Ti species distribution and hierarchical pores in TS-1: towards regeneration of TS-1 deactivated due to alkali corrosion

TS-1 deactivated in industrial cyclohexanone ammoximation can be effectively regenerated by hydrothermal treatment with TPABr and ethanolamine solution.

Highly selective 1-pentene epoxidation over Ti-MWW with modified microenvironment of Ti active sites

The hexa-coordinated Ti active sites with the piperidine molecules as ligand significantly accelerate H₂O₂ activation, which effectively improve the catalytic performance of Ti-MWW in the 1-pentene epoxidation reaction.

Lewis acidic strength controlled highly selective synthesis of oxime via liquid-phase ammoximation over titanosilicates

The Lewis acidity of titanosilicates determines oxime selectivity in ammoximation by influencing the reaction activation energy of Ti–OOH for the highly efficient formation of NH₂OH.