Observation of hysteretic magnetic phase transitions coupled with orientation motion of ions and dielectric relaxation in a one-dimensional nickel-bis-dithiolene molecule solid

Polymorph transformation in a mixed-stacking nickel-dithiolene complex with the derivative of 4,4'-bipyridinium

In this study, two polymorphs of the [1,1'-dibutyl-4,4'-bipyridinium][Ni(mnt)2] salt (1) were synthesized. The dark-green polymorph (designated as 1-g) was prepared under ambient conditions by the rapid precipitation method in aqueous solutions. Subsequently, the red polymorph (labeled as 1-r) was obtained by subjecting 1-g to ultrasonication in MeOH at room temperature. Microanalysis, infrared spectroscopy, thermogravimetry (TG), differential scanning calorimetry (DSC), and powder X-ray diffraction (PXRD) techniques were used to characterize the two polymorphs. Both 1-g and 1-r exhibit structural phase transitions: a reversible phase transition at ∼403 K (∼268 K) upon heating and 384 K (∼252 K) upon cooling for 1-g (1-r) within the temperature range below 473 K. Interestingly, on heating 1-r to 523 K, an irreversible phase transition occurred at about 494 K, resulting in the conversion of 1-r into 1-g. Relative to 1-r, 1-g represents a thermodynamically metastable phase wherein numerous high-energy conformations in butyl chains of cations are confined within the lattice owing to quick precipitation or rapid annealing from higher temperatures. Through variable-temperature single crystal and powder X-ray diffractions, UV-visible spectroscopy, dielectric spectroscopy, and DSC analyses, this study delves into the mechanism underlying phase transitions for each polymorph and the manual transformation between 1-g and 1-r as well.

A Promising Phase Change Material with Record High Ionic Conductivity over a Wide Temperature Range of a Plastic Crystal Phase and Magnetic Thermal Memory Effect

The emerging organic ion plastic crystals (OIPCs) are the most promising candidates used as solid-state electrolytes in a range of ionic devices. To endow an OIPC with additional functionality may create a new type of material for multifunctional devices. Herein, we present an ion plastic crystal, [EMIm][Ni(mnt)₂] (1; [EMIm]⁺ = 1-ethyl-3-methylimidazolium and mnt^2- = maleonitriledithiolate), and its crystal consists of twin dimeric chains of [Ni(mnt)₂]^- anions, embraced by [EMIm]⁺ cations. A crystal-to-plastic crystal transformation with a large latent heat that occurred at ∼367/337 K on heating/cooling is confirmed by the differential scanning calorimetry (DSC) technique. The plastic crystal phase in 1, characterized by variable temperature powder X-ray diffraction (PXRD) and optical microscopy images, spans a broad temperature range with ΔT ∼123/153 K on heating/cooling (DSC measurement), and the wide ΔT is relevant to an extra stable anion chain owing to the strong antiferromagnetic (AFM) interactions protecting the chain from collapse in the plastic crystal state. 1 is a single-component ion plastic crystal with a record high ion conductivity, 0.21 S·cm^-1, at 453 K. The crystal-to-plastic crystal transformation in 1 is coupled to a bistable magnetic transition to give a multi-in-one multifunctional material. This study provides a creative thought for the design of OIPCs with striking thermal, electrical, and magnetic multifunctionality.

Structural changes in MII dithione/dithiolato complexes (M = Ni, Pd, Pt) on varying the dithione functionalization

Large differences in the crystal structures of the title triads, induced by interactions exchanged by the peripheral fragments of the ligands, have been found and described through the Hirshfeld surface analysis.