Bimodal mesoporous titanium dioxide anatase films templated by a block polymer and an ionic liquid: influence of the porosity on the permeability

Enhancing the Spectroelectrochemical Performance of WO3 Films by Use of Structure-Directing Agents during Film Growth

Thin, porous films of WO3 were fabricated by solution-based synthesis via spin-coating using polyethylene glycol (PEG), a block copolymer (PIB50-b-PEO45), or a combination of PEG and PIB50-b-PEO45 as structure-directing agents. The influence of the polymers on the composition and porosity of WO3 was investigated by microwave plasma atomic emission spectroscopy, energy-dispersive X-ray spectroscopy, scanning electron microscopy, X-ray diffraction, and gas sorption analysis. The electrochromic performance of the WO3 thin films was characterized with LiClO4 in propylene carbonate as electrolyte. To analyze the intercalation of the Li+ ions, time-of-flight secondary ion mass spectrometry, and X-ray photoelectron spectroscopy were performed on films in a pristine or reduced state. The use of PEG led to networks of micropores allowing fast reversible electrochromic switching with a high modulation of the optical transmittance and a high coloration efficiency. The use of PIB50-b-PEO45 provided isolated spherical mesopores leading to an electrochromic performance similar to compact WO3, only. Optimum characteristics were obtained in films which had been prepared in the presence of both, PEG and PIB50-b-PEO45, since WO3 films with mesopores were obtained that were interconnected by a microporous network and showed a clear progress in electrochromic switching beyond compact or microporous WO3.

Comparison of In-Plane Stress Development in Sol-Gel- and Nanoparticle-Derived Mesoporous Metal Oxide Thin Films

By using an evaporation-induced self-assembly (EISA) process, mesoporous metal oxide thin films are prepared via molecular precursors undergoing a sol-gel transition or by using nanoparticle dispersions as the starting materials. Both methods are employed together with PIB₅₀-b-PEO₄₅ as the structure-directing agent to produce porous TiO₂ and ZrO₂ thin films with spherical mesopores of around 14 nm in diameter. These nanoparticle- and sol-gel-derived films were investigated in terms of the intrinsic in-plane stress development during the heat treatment up to 500 °C to evaluate the impact of solvent evaporation, template decomposition and crystallization on the mechanical state of the film. The investigation revealed the lowest intrinsic stress for the nanoparticle-derived mesoporous film, which is assigned to the combination of the relaxing effects of the utilized diblock copolymer and the interparticular gaps between the precrystalline nanoparticles. Furthermore, the residual in-plane stress was studied after annealing steps ranging from 300 to 1000 °C and cooling down to room temperature. Here, TiO₂ nanoparticle-derived mesoporous films possess a lower residual stress than the sol-gel-derived mesoporous films, while in the case of ZrO₂ films, sol-gel-derived coatings reveal the smallest residual stress. The latter is based on the lower thermal expansion coefficient of the dominant monoclinic crystal phase compared to that of the silicon substrate. Hence, the present crystal structure has a strong influence on the mechanical state. The observation in this study helps to further understand the stress-related mechanical properties and the formation of mesoporous metal oxides.

Tuning Pore Dimensions of Mesoporous Inorganic Films by Homopolymer Swelling

The functionality and applications of mesoporous inorganic films are closely linked to their mesopore dimensions. For material architectures derived from a block copolymer (BCP) micelle coassembly, the pore size is typically manipulated by changing the molecular weight corresponding to the pore-forming block. However, bespoke BCP synthesis is often a costly and time-consuming process. An alternative method for pore size tuning involves the use of swelling agents, such as homopolymers (HPs), which selectively interact with the core-forming block to increase the micelle size in solution. In this work, poly(isobutylene)-block-poly(ethylene oxide) micelles were swollen with poly(isobutylene) HP in solution and coassembled with aluminosilicate sol with the aim of increasing the resulting pore dimensions. An analytical approach implementing spectroscopic ellipsometry (SE) and ellipsometric porosimetry (EP) alongside atomic force microscopy (AFM) and small-angle X-ray scattering (SAXS) in transmission and grazing-incidence (GISAXS) modes enabled us to study the material evolution from solution processing through the manifestation of the mesoporous inorganic film after BCP removal. The in-depth SE/EP analysis evidenced an increase of more than 45% in mesopore diameter with HP swelling and a consistent scaling of the overall void volume and number of pores. Importantly, our analytical toolbox enabled us to study the effect of swelling on the connecting necks between adjacent pores, with observed increases as high as ≈35%, offering novel pathways to sensing, electrochemical, and other mass-transfer-dependent applications.

TiO2 mesoporous thin film architecture as a tool to control Au nanoparticles growth and sensing capabilities

In this paper, a systematic study regarding the effect of the mesoporous structure over Au nanoparticles (NPs) growth inside and through the pores of mesoporous TiO2 thin films (MTTFs) is presented, and the effect of such characteristics over the composites' sensing capabilities is evaluated. Highly stable MTTFs with different pore diameters (range: 4-8 nm) and pore arrangements (body- and face-centered cubic) were synthesized and characterized. Au NPs were grown inside the pores, and it was demonstrated-through a careful physicochemical characterization-that the amount of incorporated Au and NP size depends on the pore array; being higher for bigger pore diameters and face-centered cubic structures. The same structure allows the growth of more and longer tips over Au NPs deposited at the thin film-substrate interface. Finally, to confirm the effect of the structural characteristics of the composites over their possible applications, the materials were tested as surface-enhanced Raman scattering (SERS)-based substrates. The composites with a higher amount of Au and more ramified NPs were the ones that presented better sensitivity in the detection of a probe molecule (4-nitrothiophenol). Overall, this work demonstrates that the pore size and ordering in MTTFs determine the materials' accessibility and connectivity, and therefore, have a clear impact on their potential applications.

In-plane stress development in mesoporous thin films

Ordered mesoporous thin films of TiO2 and CexZr1-xO2 (x = 0, 0.5, 1) were prepared via an evaporation-induced self-assembly (EISA) process and subsequently investigated in terms of the developing intrinsic and residual in-plane stress. These mechanical properties were determined by the curvature method, which is based on the determination of the deflection of light due to concave or convex bending of the films on a substrate. The films were investigated with regard to the intrinsic stress during heat treatment up to 500 °C and to the residual stress at room temperature for several annealing temperatures. Following this strategy, the influence of the decomposition of a block copolymer template on the intrinsic stress as well as the pore collapsing on the residual stress was analyzed. Nanoporous TiO2 thin films were prepared using two different block copolymers (PIB50-b-PEO45 and Pluronic® F127). A comparison between the templated and non-templated TiO2 films showed the lowest intrinsic and residual stress for the ordered mesoporous material prepared with PIB50-b-PEO45 indicating that the distributed polymer and the corresponding mesopores act as relaxing agents for the system. This was verified by mesoporous CexZr1-xO2 (x = 0, 0.5, 1) thin films showing a comparable behavior in terms of the experienced intrinsic stress. This work reveals an increase in the residual in-plane stress during pore collapse, which lays the foundation for further understanding of the stress-related mechanical properties of mesoporous thin films.

Liquid crystal self-assembly of halloysite nanotubes in ionic liquids: a novel soft nanocomposite ionogel electrolyte with high anisotropic ionic conductivity and thermal stability

We report a novel class of liquid crystalline (LC) nanohybrid ionogels fabricated via self-assembly of natural halloysite nanotubes (HNTs) in ionic liquids (ILs). The obtained ionogels are very stable and nonvolatile and show LC phases over a wide temperature range. Remarkably, the nanocomposite ionogels exhibit high anisotropic ionic conductivity after shear, and their room temperature ionic conductivity can reach 3.8 × 10(-3) S cm(-1) for aligned nanotubes perpendicular to the electrode even when the HNTs content increases to 40 wt%, which is 380 times higher than that obtained for aligned nanotubes parallel to the electrode, which is 1.0 × 10(-5) S cm(-1). Crucially, the obtained LC nanocomposite ionogels have very high thermal stability, which can sustain 400 °C thermal treatment. The findings will promote the development of novel nanocomposite ionogel electrolytes with faster ion transport and larger anisotropic conductivity.

Tailored Synthesis of Porous TiO₂ Nanocubes and Nanoparallelepipeds with Exposed {111} Facets and Mesoscopic Void Space: A Superior Candidate for Efficient Dye-Sensitized Solar Cells

Anatase TiO2 nanocubes and nanoparallelepipeds, with highly reactive {111} facets exposed, were developed for the first time through a modified one pot hydrothermal method, through the hydrolysis of tetrabutyltitanate in the presence of oleylamine as the morphology-controlling capping-agent and using ammonia/hydrofluoric acid for stabilizing the {111} faceted surfaces. These nanocubes/nanoparallelepipeds were characterized by X-ray diffraction (XRD), transmission electron microscopy (TEM), high resolution transmission electron microscopy (HRTEM) and high angle annular dark-field scanning TEM (HAADF-STEM). Accordingly, a possible growth mechanism for the nanostructures is elucidated. The morphology, surface area and the pore size distribution of the TiO2 nanostructures can be tuned simply by altering the HF and ammonia dosage in the precursor solution. More importantly, optimization of the reaction system leads to the assembly of highly crystalline, high surface area, {111} faceted anatase TiO2 nanocubes/nanoparallelepipeds to form uniform mesoscopic void space. We report the development of a novel double layered photoanode for dye sensitized solar cells (DSSCs) made of highly crystalline, self-assembled faceted TiO2 nanocrystals as upper layer and commercial titania nanoparticles paste as under layer. The bilayered DSSC made from TiO2 nanostructures with exposed {111} facets as upper layer shows a much higher power conversion efficiency (9.60%), than DSSCs fabricated with commercial (P25) titania powder (4.67%) or with anatase TiO2 nanostructures having exposed {101} facets (7.59%) as the upper layer. The improved performance in bilayered DSSC made from TiO2 nanostructures with exposed {111} facets as the upper layer is attributed to high dye adsorption and fast electron transport dynamics owing to the unique structural features of the {111} facets in TiO2. Electrochemical impedance spectroscopy (EIS) measurements conducted on the cells supported these conclusions, which showed that the bilayered DSSC made from TiO2 nanostructures with exposed {111} facets as the upper layer possessed lower charge transfer resistance, higher electron recombination resistance, longer electron lifetime and higher collector efficiency characteristics, compared to DSSCs fabricated with commercial (P25) titania powder or with anatase TiO2 nanostructures having exposed {101} facets as the upper layer.