Aluminium doped ZnO nanostructures for efficient photodegradation of indigo carmine and azo carmine G in solar irradiation

Aluminium doped zinc oxide (AZO) nanomaterials (AlxZn1-xO) with x fraction varying as 0.02 and 0.04 were synthesized using the auto-combustion method using glycine as a fuel. The synthesized catalysts were characterized with X-ray diffraction (XRD), UV–Visible Spectroscopy (UV–Vis), Raman spectroscopy, Photoluminescence (PL) spectroscopy, and High Resolution Transmission Electron Microscopy (HR-TEM). XRD results showed that synthesized materials possessed good crystallinity, while UV–VIS was employed to find the band gaps of synthesized materials. Raman was used to determine the vibrational modes in the synthesized nanoparticles, while TEM analysis was performed to study the morphology of the samples. Industrial effluents such as indigo carmine and azo carmine G were used to test the photodegradation ability of synthesised catalysts. Parameters such as the effect of catalyst loading, dye concentration and pH were studied. The reduction in crystallite size, band gap and increased lattice strain for the 4% AZO was the primary reason for the degradation in visible irradiation, degrading 97 and 99% equimolar concentrations of indigo carmine and azo carmine G in 140 min. The Al doped ZnO was found to be effective in faster degradation of dyes as compared to pure ZnO in presence of natural sunlight.

Apple-like Zinc-Oxide Mesocrystals as Robust and Versatile Photocatalysts for Efficient Degradation of Eight Different Organic Dyes

The discovery of efficient photocatalysts is a promising key approach to solve the environmental crisis caused by hazardous organic dyes. Herein, we have for the first time created ZnO mesocrystals with a novel apple-like morphology. We have developed a one-pot biomineralization route to synthesize ZnO nanostructures at room temperature by using the rod-like protein collagen as the template. The shape of ZnO mesocrystals can be conveniently tuned from fusiform-like and kiwi-like to orange-like, apple-like, and snack-like structures. The apple-like ZnO mesocrystals show a significantly better photodegradation efficiency than the commercial ZnO powder as well as other nanostructured ZnO materials for both rhodamine B (RhB) and methyl orange (MO). Furthermore, the apple-like zinc-oxide mesocrystals can degrade all of the tested eight different types of organic dyes (RhB, rhodamine 6G, methylene blue, Coomassie brilliant blue R250, BPB, MO, Li Chunhong S, and carmine) simply under the exposure of sunlight, demonstrating their superior photodegradation prowess, environmental amiability, and energy-saving features. The novel robust and versatile photocatalyst has greatly advanced our abilities for the elimination of organic dyes. The green, one-pot strategy provides a convenient method for the construction of novel metal-oxide nanostructures with promising applications in environmental protection.

On-chip grown ZnO nanosheet-array with interconnected nanojunction interfaces for enhanced optoelectronic NO2 gas sensing at room temperature

Herein, we demonstrated the on-chip growth of nanostructured ZnO films with abundant nanojunctions for the fabrication of high-performance optoelectronic NO₂ sensors. A fast solution approach allowed the controllable growth of ZnO nanorod- and nanosheet-arrays directly on flexible substrates, which were endowed with abundant nanojunctions. Electron microscopy observations revealed the existence of two types of the nanojunction interfaces, i.e., the attached and interconnected interfaces within the nanostructure networks. Compared with the attached nanorods, the optoelectronic NO₂ sensors based on interconnected ZnO nanosheets showed higher responses and faster response/recovery rates under UV illumination at room temperature. The responses of the nanosheet-based sensor ranged from 28% to 610% toward NO₂ concentrations of 10 ppb to 1000 ppb. Moreover, the optoelectronic sensors exhibited excellent reversibility, and mechanical and long-term stabilities along with low detection limits. The enhanced optoelectronic NO₂ sensing properties of the interconnected ZnO nanosheets could be attributed to different types of nanojunction interfaces, which played a key role in modulating the interfacial potential barrier heights of the nanojunctions according to the surface depletion model. The presently developed strategy of nanojunction interface engineering is expected to have wide interest for semiconductor-based sensor applications.

Facile Fabrication of Multifunctional ZnO Urchins on Surfaces

Functional ZnO nanostructured surfaces are important in a wide range of applications. Here we report the simple fabrication of ZnO surface structures at near room temperature with morphology resembling that of sea urchins, with densely packed, μm-long, tapered nanoneedles radiating from the urchin center. The ZnO urchin structures were successfully formed on several different substrates with high surface density and coverage, including silicon (Si), glass, polydimethylsiloxane (PDMS), and copper (Cu) sheets, as well as Si seeded with ZnO nanocrystals. Time-resolved SEM revealed growth kinetics of the ZnO nanostructures on Si, capturing the emergence of “infant” urchins at the early growth stage and subsequent progressive increases in the urchin nanoneedle length and density, whilst the spiky nanoneedle morphology was retained throughout the growth. ε-Zn(OH)2 orthorhombic crystals were also observed alongside the urchins. The crystal structures of the nanostructures at different growth times were confirmed by synchrotron X-ray diffraction measurements. On seeded Si substrates, a two-stage growth mechanism was identified, with a primary growth step of vertically aligned ZnO nanoneedle arrays preceding the secondary growth of the urchins atop the nanoneedle array. The antibacterial, anti-reflective, and wetting functionality of the ZnO urchins—with spiky nanoneedles and at high surface density—on Si substrates was demonstrated. First, bacteria colonization was found to be suppressed on the surface after 24 h incubation in gram-negative Escherichia coli (E. coli) culture, in contrast to control substrates (bare Si and Si sputtered with a 20 nm ZnO thin film). Secondly, the ZnO urchin surface, exhibiting superhydrophilic property with a water contact angle ~ 0°, could be rendered superhydrophobic with a simple silanization step, characterized by an apparent water contact angle θ of 159° ± 1.4° and contact angle hysteresis ∆θ < 7°. The dynamic superhydrophobicity of the surface was demonstrated by the bouncing-off of a falling 10 μL water droplet, with a contact time of 15.3 milliseconds (ms), captured using a high-speed camera. Thirdly, it was shown that the presence of dense spiky ZnO nanoneedles and urchins on the seeded Si substrate exhibited a reflectance R < 1% over the wavelength range λ = 200–800 nm. The ZnO urchins with a unique morphology fabricated via a simple route at room temperature, and readily implementable on different substrates, may be further exploited for multifunctional surfaces and product formulations.

Nanoplate-assembled hierarchical cake-like ZnO microstructures: solvothermal synthesis, characterization and photocatalytic properties

Hierarchical nanoplate-assembled cake-like ZnO microstructures were synthesized via a DMF-assisted solvothermal route by using NH₄BF₄ as a fluoride source.

Hierarchical ZnO Nanosheet-Nanorod Architectures for Fabrication of Poly(3-hexylthiophene)/ZnO Hybrid NO2 Sensor

A facile one-step solution method has been developed here to fabricate hierarchical ZnO nanosheet-nanorod architectures for compositing with poly(3-hexylthiophene) (P3HT) for fabricating a hybrid NO2 sensor. The hierarchical ZnO nanosheet-nanorod architectures were controllably synthesized by aging the solutions containing 0.05 mol·L(-1) Zn(2+) and 0.33 mol·L(-1) OH(-) at 60 °C through a metastable phase-directed mechanism. The concentration of OH(-) played a huge role on the morphology evolution. When the [OH(-)] concentration was decreased from 0.5 to 0.3 mol·L(-1), the morphology of the ZnO nanostructures changed gradually from monodispersed nanorods (NR) to nanorod assemblies (NRA), and then to nanosheet-nanorod architectures (NS-NR) and nanosheet assemblies (NSA), depending on the formation of various metastable, intermediate phases. The formation of NS-NR included the initial formation of ZnO nanosheets/γ-Zn(OH)2 mixed intermediates, followed by the dissolution of Zn(OH)2, which served as soluble zinc source. Soluble Zn(OH)2 facilitated the dislocation-driven secondary growth of ZnO nanorod arrays on the primary defect-rich nanosheet substrates. Hybrid sensors based on composite films composed of P3HT and the as-prepared ZnO nanostructures were fabricated for the detection of NO2 at room temperature. The P3HT/ZnO NS-NR bilayer film exhibited not only the highest sensitivity but also good reproducibility and selectivity to NO2 at room temperature. The enhanced sensing performance was attributed to the formation of the P3HT/ZnO heterojunction in addition to the enhanced adsorption of NO2 by NS-NR ZnO rich in oxygen-vacancy defects.

Shape control of inorganic nanoparticles from solution

Inorganic materials with controllable shapes have been an intensely studied subject in nanoscience over the past decades. Control over novel and anisotropic shapes of inorganic nanomaterials differing from those of bulk materials leads to unique and tunable properties for widespread applications such as biomedicine, catalysis, fuels or solar cells and magnetic data storage. This review presents a comprehensive overview of shape-controlled inorganic nanomaterials via nucleation and growth theory and the control of experimental conditions (including supersaturation, temperature, surfactants and secondary nucleation), providing a brief account of the shape control of inorganic nanoparticles during wet-chemistry synthetic processes. Subsequently, typical mechanisms for shape-controlled inorganic nanoparticles and the general shape of the nanoparticles formed by each mechanism are also expounded. Furthermore, the differences between similar mechanisms for the shape control of inorganic nanoparticles are also clearly described. The authors envision that this review will provide valuable guidance on experimental conditions and process control for the synthesis of inorganic nanoparticles with tunable shapes in the solution state.

Synthesis of ultra-long hierarchical ZnO whiskers in a hydrothermal system for dye-sensitised solar cells

Ultra-long hierarchical ZnO whiskers (>100 μm) with tunable lengths through one-pot hydrothermal process have been demonstrated.

Pathway of zinc oxide formation by seed-assisted and controlled double-jet precipitation

ZnO can be well formed in a short time at room temperature via seed-assisted and controlled double-jet precipitation.

Electronic structure and optical properties of Zn(OH)2: LDA+U calculations and intense yellow luminescence

Assigned U values in the LDA+U calculations should assure an appropriate overlap of the p−d states.

Supersaturation-induced hydrothermal formation of α-CaSO4·0.5H2O whiskers

Supersaturation-induced fast transformation from CaSO₄·2H₂O to α-CaSO₄·0.5H₂O was observed and the process followed the dissolution–precipitation and homogeneous nucleation mechanism according to classical nucleation theory.