Preparation of Eu(III) Complexes Containing Maleopimaric Acid Anhydride with Ultra-narrow and Efficient Fluorescence Emission for High Determination on Gallic Acid in Acetonitrile Solution

Two novel Eu(III) complexes constructed by maleopimaric acid anhydride (MPA) and 2,2'-bipyridyl (Bpy) / 1, 10-phenanthroline (Phen), named as MPA-Bpy-Eu / MPA-Phen-Eu, have been synthesized by a one-step precipitation method. FTIR, UV, TG, elemental analysis, XPS, and ESI-MS revealed the successful coordination of Eu(III) ions with MPA and Bpy / Phen through Eu-O and Eu-N bonds, respectively. Introducing MPA into coordinate structure increased the electron cloud density in 3d_5/2 orbit of Eu(III) ions, enhanced the absolute quantum yields of MPA-Bpy-Eu (89.27%) and MPA-Phen-Eu (94.41%), and decreased the full width at half maxima of ⁵D₀ → ⁷F₂ transitions of MPA-Bpy-Eu (2.23 nm) and MPA-Phen-Eu (2.93 nm), respectively. The fluorescence quenching experiments showed that there was a good linear relationship between the relative fluorescence intensity of MPA-Bpy-Eu and gallic acid (GA) concentration in acetonitrile solution in the range of 0 to 8.41 × 10^-2 mM. The results of UV-vis spectra, the fluorescence lifetimes, and the quantum yields demonstrated that the dynamic quenching model played a major role in the quenching process of GA on MPA-Bpy-Eu. The quenching process of GA on MPA-Phen-Eu involved dual fluorescence quenching mechanistic pathways, including static and dynamic models.

Effect of the Titanium Self-Intercalation on the Electronic Structure of TiSe2

The effect of the superstoichiometric Ti intercalation on the electronic structure of TiSe₂ was studied by using X-ray photoelectron spectroscopy in nonresonant and resonant modes along with the DOS (density of states) calculations. It was shown that the presence of the Ti atoms in the interlayer space leads to the formation of the Ti 3d_z²/Ti 3d_z² hybridized band between the Ti atoms in the regular lattice positions and Ti atoms in the interlayer space. The charge transfer to the conduction band was not observed in this case.

Specific features of the electronic structure of CoxTiSe2 according to the resonant photoemission data

The effect of atomic ordering in the Co sublattice on the electronic structure of the Co_xTiSe₂ compounds has been studied using a complex of spectral techniques – XPS, XAS, and ResPES, along with theoretical calculations of the total and partial DOS.

Electrospun Poly(acrylic acid)/Silica Hydrogel Nanofibers Scaffold for Highly Efficient Adsorption of Lanthanide Ions and Its Photoluminescence Performance

Combined with the features of electrospun nanofibers and the nature of hydrogel, a novel choreographed poly(acrylic acid)-silica hydrogel nanofibers (PAA-S HNFs) scaffold with excellent rare earth elements (REEs) recovery performance was fabricated by a facile route consisting of colloid-electrospinning of PAA/SiO2 precursor solution, moderate thermal cross-linking of PAA-S nanofiber matrix, and full swelling in water. The resultant PAA-S HNFs with a loose and spongy porous network structure exhibited a remarkable adsorption capacity of lanthanide ions (Ln(3+)) triggered by the penetration of Ln(3+) from the nanofiber surface to interior through the abundant water channels, which took full advantage of the internal adsorption sites of nanofibers. The effects of initial solution pH, concentration, and contact time on adsorption of Ln(3+) have been investigated comprehensively. The maximum equilibrium adsorption capacities for La(3+), Eu(3+), and Tb(3+) were 232.6, 268.8, and 250.0 mg/g, respectively, at pH 6, and the adsorption data were well-fitted to the Langmuir isotherm and pseudo-second-order models. The resultant PAA-S HNFs scaffolds could be regenerated successfully. Furthermore, the proposed adsorption mechanism of Ln(3+) on PAA-S HNFs scaffolds was the formation of bidentate carboxylates between carboxyl groups and Ln(3+) confirmed by FT-IR and XPS analysis. The well-designed PAA-S HNFs scaffold can be used as a promising alternative for effective REEs recovery. Moreover, benefiting from the unique features of Ln(3+), the Ln-PAA-S HNFs simultaneously exhibited versatile advantages including good photoluminescent performance, tunable emission color, and excellent flexibility and processability, which also hold great potential for applications in luminescent patterning, underwater fluorescent devices, sensors, and biomaterials, among others.