Removal of ethyl mercaptan from gas streams using chromium modified hexaniobate nanotubes

In this study, chromium modified hexaniobate nanotubes with high dispersion of the chromium species were first prepared by the ion exchange–flocculation–calcination process for removal of C2H5SH.

Influence of the preparation conditions on the morphology and photocatalytic performance Pt-modified hexaniobate composites

The preparation of lamellar nanostructures through exfoliation of stacked niobates is an interesting approach to the development of photocatalysts for energy conversion and environmental remediation. These materials exhibit a rich surface chemistry and several nanocomposites can be produced through intercalation or impregnation of suitable precursors. In this work, the influence of the physico-chemical preparation conditions on the photocatalytic activity of Pt-hexaniobate nanocomposites was investigated aiming at the establishment of the main factors that control their photoreactivities. Modification of hexaniobate layers were carried out by adsorption and impregnation methods, using [Pt(NH₃)₄]Cl₂ (Pt1) and H₂PtCl₆ (Pt2), respectively. The addition of platinum precursors (1% wt.) were performed in the presence of the exfoliating agent tert-butylammonium hydroxide, sNb, or after acidic precipitation followed by resuspension in plain water, eNb. All samples were submitted to photoirradiation to reduce the platinum precursors and the effect of a previous thermal treatment was also evaluated. It was observed that H₂ evolution from aqueous methanol solutions is more favored on hexaniobate nanosheets (eNb-Pt1 and eNb-Pt2) instead of scrolled layers (sNb-Pt1 and sNb-Pt2), independent on the platinum precursor. Moreover, residual tert-butylammonium can act as hole scavenger and decrease the degradation rates for methanol oxidation in sNb samples. The curled layers observed for sNb samples seem to favor the photodegradation of cationic species, such as methylene blue. Thermal treatment at 500 °C leads to morphological changes with a decrease of the specific surface area due to restacking of the individual layers along with some curling. As a result, the H₂ evolution rates strongly decreases in relation to the non-sintered samples, suggesting that the 'soft' photoreduction of platinum precursors is the best method for preparation of these photocatalysts. The correlations between the preparation conditions and the photocatalytic activity for different photoreactions can allow the development of optimized materials for specific applications.

Soft chemistry of ion-exchangeable layered metal oxides

Disassembly and re-assembly of layered metal oxides by soft chemical approaches can be used to tailor functionalities in artificial photosynthesis, energy storage, optics, and piezoelectrics.

Synthesis, characterization and enhanced visible-light photocatalytic activity of novel NiO/HTi2NbO7nanocomposite

The decreased electron–hole recombination rate of the NiO/HTi₂NbO₇nanocomposite plays a crucial role in improving visible-light photocatalytic activity.