Single-step synthesis of ternary metal chalcogenides (sf-CuInS2 and sf-CuInSe2) stripped off the organic cover and their use as a catalyst for symmetric Glaser-Hay coupling reactions

Generally, inorganic nano/microparticles produced by chemical routes are covered by organic surfactants or polymers to control their agglomeration during their synthesis. However, these surfactants and polymers negatively affect their catalytic activity because these molecules mask the surface. This work presents the synthesis of surfactant-free CuInS2 and CuInSe2 (sf-CuInS2 and sf-CuInSe2) nano/microparticles through simple reactions without surfactant or polymer coatings using LiBH4 under a thermodynamically favourable condition. These reactions are rare observations of a single-step process to produce ternary metal chalcogenides without any template assistance. We have also demonstrated efficient catalysis by sf-CuInS2 nanoparticles in the coupling reaction of substituted phenylacetylenes. We tested it as catalysts in dimerizing 1,3-diyne derivatives while using 8-diazabicyclo[5.4.0]undec-7-ene (DBU) as the base. These Glassar-Hay coupling reactions are conducted at room temperature in acetonitrile (4-7 h, depending on the substrate) using 10 mg of sf-CuInS2. The maximum yield obtained in these reactions is 97%, while the catalyst is reusable for five cycles with little difference in its ability to catalyse. The effectiveness of the catalyst is credited to the availability of a free catalytic surface.

Lead ethyl dithiocarbamates: efficient single-source precursors to PbS nanocubes

Lead ethyl dithiocarbamates have been successfully used as single-source precursors for the deposition of PbS using spin coating followed by annealing at moderate temperatures. The thin films were characterized using a powder X-ray diffractometer and were found to be face-centred cubic with the (200) plane being the most preferred orientation. Scanning electron microscopy images showed the formation of well-defined cubes. Optical band gaps of PbS thin films were estimated using Tauc plots as 0.72, 0.73 and 0.77 eV at annealing temperatures of 250, 300 and 400°C. These band gaps were all blue shifted from the bulk value of 0.41 eV. Energy-dispersive X-ray analysis was used to determine the composition of the thin films which showed an approximately 1 : 1 Pb to S ratio.

Structural control of InP/ZnS core/shell quantum dots enables high-quality white LEDs

Herein, we demonstrate that the structural and optical control of InP-based quantum dots (QDs) can lead to high-performance light-emitting diodes (LEDs). Zinc sulphide (ZnS) shells passivate the InP QD core and increase the quantum yield in green-emitting QDs by 13-fold and red-emitting QDs by 8-fold. The optimised QDs are integrated in the liquid state to eliminate aggregation-induced emission quenching and we fabricated white LEDs with a warm, neutral and cool-white appearance by the down-conversion mechanism. The QD-functionalized white LEDs achieve luminous efficiency (LE) up to 14.7 lm W^-1 and colour-rendering index up to 80. The structural and optical control of InP/ZnS core/shell QDs enable 23-fold enhancement in LE of white LEDs compared to ones containing only QDs of InP core.